Picosecond Laser Shock Peening of Nimonic 263 at 1064 nm and 532 nm Wavelength
(MDPI, Basel, 2016)
The paper presents a study on the surface modifications of nickel based superalloy Nimonic 263 induced by laser shock peening (LSP) process. The process was performed by Nd3+:Yttrium Aluminium Garnet (YAG) picosecond laser ...
Stringer effect on fatigue crack propagation in A2024-T351 aluminum alloy welded joint
(Elsevier Sci Ltd, Oxford, 2017)
This paper describes fatigue crack growth in a friction stir welded T joints made of aluminum alloy A2024-T351 under three point bending loads. For this purpose, three dimensional homogeneous isotropic model is used to ...
Experimental investigations of flow distribution in coolant system of Helium-Cooled-Pebble-Bed Test Blanket Module
(Elsevier Science Sa, Lausanne, 2016)
This paper deals with investigations of flow distribution in the coolant system of the Helium-Cooled Pebble -Bed Test Blanket Module (HCPB TBM) for ITER. The investigations have been performed by manufacturing and testing ...
Numerical analysis of fatigue crack growth of hip implant
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Fatigue crack growth in hip implant has been analysed using the extended finite element method. Toward this aim, the three-dimensional finite element model is created and used in ABAQUS and Morfeo/crack add-in for ABAQUS ...
Effects of a low-Shrinkage methacrylate monomer and monoacylphosphine oxide photoinitiator on curing efficiency and mechanical properties of experimental resin-based composites
(Elsevier, Amsterdam, 2016)
This study investigated the degree of conversion, depth of cure, Vickers hardness, flexural strength, flexural modulus and volumetric shrinkage of experimental composite containing a low shrinkage monomer FIT-852 (FIT; ...
Laser Processing of Ni-Based Superalloy Surfaces Susceptible to Stress Concentration
(MDPI, Basel, 2021)
Reliable and resilient constructions are basic for ensuring the safety of various structures. The superalloys are used as constructive materials due to their superb mechanical properties and endurance. However, even these ...
Determination of optimum wing spar cross section for maximum fatigue life
(Elsevier Sci Ltd, Oxford, 2019)
Shape optimisation is a nowadays-standard requirement in the design of lightweight structural components. In this paper, optimisation of I-beam cross-section of integral aluminium 2024-T3 wing spar is presented, taking the ...
Numerical and Experimental Investigations of Fracture Behaviour of Welded Joints with Multiple Defects
(MDPI, Basel, 2021)
Current standards related to welded joint defects (EN ISO 5817) only consider individual cases (i.e., single defect in a welded joint). The question remains about the behaviour of a welded joint in the simultaneous presence ...
Butt welded joints assessment after fire exposure
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The need of in service life of a steel structure after being exposed to fire raises the problem of strengthening or replacement of some structural elements. In many cases, after structural safety assessment, fire exposed ...
Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...