Experimental investigation of temperature and strain-rate behaviour of Ti3Al-Nb alloy
(Scientific Society for Mechanical Engineering, 2011)
Welded penstock, produced of high-strength steel and application of fracture mechanics parameters to structural integrity assessment
(Springer, Dordrecht, 2008)
Application of high-strength steel for welded penstock increased the probability of crack-like defects and in welded joint. Structural integrity assessment procedure is presented and applied to welded penstock produced of ...
Modelling of ductile crack growth in welded joints using micromechanical failure criterion
(17th European Conference on Fracture 2008: Multilevel Approach to Fracture of Materials, Components, 2008)
In this paper, ductile crack growth in strength mismatched welded joints is considered. High-strength low-alloyed (HSLA) steel in quenched and tempered condition is used as the base metal. Two different fillers are selected ...
Fracture mechanics and non-destructive testing for structural integrity assessment
(Trans Tech Publications Ltd, Durnten-Zurich, 2009)
Fracture mechanics parameters can be applied for the analysis of failures of structures, and also for prevention of failures when defects in a structure are detected and defined. The approach is presented through stages: ...
Structural integrity assessment by local approach to fracture
(Kluwer Academic Publishers, 2006)
Evaluation of damage of steam pipeline steel using local approach to fracture
(American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP, 2008)
In the paper, the level of damage of steam pipeline steel after about 100,000 hours at 540°C (1004 °F) under pressure of 42 bars (609 PSI) is analyzed. Material degradation is estimated using a combined experimental and ...
Analysis of loading steel structure of bucket wheel excavator by stress condition measuring
(Institute of Mechanical Engineering, 2009)
Micromechanical analysis of constraint effect on fracture initiation in strength mismatched welded joints
(Trans Tech Publications Ltd, 2007)
In this paper the micromechanical approach to ductile fracture was applied in a study of constraint effect on crack growth initiation in mismatched welded joints. The single-edged notched bend specimens (precrack length a ...
Crack tip strain on ship and in situ measurement in shipyards
(IFAC Secretariat, 2007)
The paper presents the application extent of procedures for measurement deformations on ships. The actual deformation distribution was measured on the surface of the specimen by the optical grating method (OGM) parallel ...
Numerical and analytical modeling of elastic-plastic fracture mechanics parameters
(Trans Tech Publications Ltd, 2007)
Structural integrity and service reliability depend on the fracture resistance of a material. Cracks in the material are the locations of stress concentration, and elastic-plastic deformation can occur causing the development ...