Failures of multifunctional bulkhead caused by high gradient of temperature, pressure and speed of rotation
(Pergamon-Elsevier Science Ltd, Oxford, 2018)
The multifunctional bulkhead is an assembly which divides the compressor and turbine space (cold and very hot area) in the gas-generator for turbo-jet and turbo-haft engines. The loads of this bulkhead present an interaction ...
Hydrogen damage of steels: A case study and hydrogen embrittlement model
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
Many efforts have been made to understand the effects of hydrogen on steels, resulting in an abundance of theoretical models and papers. However, a fully developed and practically applicable predictive physical model still ...
Influence of welded joint microstructures on fatigue behaviour of specimens with a notch in the heat affected zone
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, the results of determining the Paris law coefficients, C and m, are presented, based on the experimental data obtained by three-point bending testing of 8 welded joint specimens. The specimens were taken ...
Fracture mechanics and fatigue crack propagation in armor steel welds
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The welding process of armor steel is a complex process due to possible welding faults appearing in all zones of weld metal joint in the form of cracks and pores, as results of high percentage of carbon in the base metal. ...
Numerical simulation of fatigue crack propagation: A case study of defected steam pipeline
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In order to prevent the premature failure of steam pipeline produced of molybdenum-vanadium steel, the experimental tests were performed to measure fracture toughness and to determine the mechanical behaviour of cracked ...
Fatigue fracture analysis of helicopter landing gear cross tube
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
This paper presents the failure analysis results of the helicopter skid landing gear. The helicopter skid landing gear fractured while the helicopter was on the ground at the airport. The aft cross tube of the landing gear ...
Editorial - Damage, cracks and failure analysis
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
The 1st Virtual European Conference on Fracture (VECF1) has gathered more than 300 researchers from all over the world. They have presented more 320 papers, including 9 plenary lectures in the scope of the main VECF1 topics. ...
Butt welded joints assessment after fire exposure
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The need of in service life of a steel structure after being exposed to fire raises the problem of strengthening or replacement of some structural elements. In many cases, after structural safety assessment, fire exposed ...
Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...
Experimental and numerical research on the failure of railway vehicles coupling links
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
Two modes of failure are analysed for coupling links, the mechanical connections that transmit traction forces between vehicles along the length of a train. Coupling links are designed to withstand the dynamic loads in ...