Probability distribution on cleavage fracture in function of Jc for reactor ferritic steel in transition temperature region
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
This paper presents the results and methods used for determining of probability of cleavage fracture toughness of ferritic reactor steel in transition temperature area. The steel tested in this study is steel know as ...
Tie-rods of the bucket wheel excavator slewing superstructure: A study of the eye plate stress state
(Elsevier Sci Ltd, Oxford, 2020)
Tie-rods of the bucket wheel and counterweight booms are vital parts of the bucket wheel excavator slewing superstructure. This paper is dedicated to the problem of identifying the stress state of the critical cross-section ...
Multi-objective design optimization strategies for small-scale vertical-axis wind turbines
(Springer, New York, 2016)
Extracting energy from wind has been an interesting and serious topic over the last few decades and a lot of work has been done on the subject. This paper discusses in detail possible approaches to optimization of a somewhat ...
Life Cycle Impact Assessment of Miscanthus Crop for Sustainable Household Heating in Serbia
(MDPI, Basel, 2018)
This paper investigates the environmental impacts and energy benefits of the cultivation of Miscanthus (Miscanthus x giganteus Greef et Deu.), in order to initiate its use in sustainable household heating in the Republic ...
Hydrogen Embrittlement of Industrial Components: Prediction, Prevention, and Models
(Natl Assoc Corrosion Eng, Houston, 2016)
Hydrogen embrittlement is a common, dangerous, and poorly understood cause of failure in many metal alloys. In practice, it is observed that different types of damage to industrial components have been tied to the presence ...
The synergistic action and interplay of hydrogen embrittlement mechanisms in steels and iron: Localized plasticity and decohesion
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Component failures due to the hydrogen embrittlement (HE) were observed in different industrial systems, including high-pressure hydrogen storage tanks, aircraft components, high-strength alloy components, and high-strength ...
Fatigue crack growth in locking compression plates
(Elsevier Sci Ltd, Oxford, 2022)
Fatigue crack growth in orthopaedic locking compression plates (LCP), under four-point bending, has been simulated by the extended finite element method (xFEM) to assess LCP optimal geometry in respect to remaining life. ...
Ergonomic design of crane cabin interior: The path to improved safety
(Elsevier Science Bv, Amsterdam, 2015)
Many procedures in the development process of crane cabins today are still based on the specific experience of manufacturers and historical guidelines. It is not surprising that they fail to meet the needs of a large ...
Fatigue crack paths in light aircraft wing spars
(Elsevier Sci Ltd, Oxford, 2019)
Different cracks paths in three different wing spar designs are analysed (differential, integral and optimized integral) to explore how those cracks paths affect fatigue life estimation. First, numerical analysis was carried ...