Fatigue crack growth in a structure exposed to high temperature
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
The exhaust nozzle, made of titanium, is the part of a jet engine where the final expansion of the hot gas from the turbine occurs and where the speed of the exhaust gas is further increased to create thrust. During the ...
Determination of optimum wing spar cross section for maximum fatigue life
(Elsevier Sci Ltd, Oxford, 2019)
Shape optimisation is a nowadays-standard requirement in the design of lightweight structural components. In this paper, optimisation of I-beam cross-section of integral aluminium 2024-T3 wing spar is presented, taking the ...
Numerical simulation of "Hall 1 of the Belgrade Fair"
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
This paper involves the analytical and numerical calculations of the the largest pre-stressed concrete free-standing structure in the world - the Dome of the "Hall 1 of the Belgrade Fair", designed by a well-known Serbian ...
Numerical analysis of fatigue crack growth of hip implant
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Fatigue crack growth in hip implant has been analysed using the extended finite element method. Toward this aim, the three-dimensional finite element model is created and used in ABAQUS and Morfeo/crack add-in for ABAQUS ...
Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...
Effects of a low-Shrinkage methacrylate monomer and monoacylphosphine oxide photoinitiator on curing efficiency and mechanical properties of experimental resin-based composites
(Elsevier, Amsterdam, 2016)
This study investigated the degree of conversion, depth of cure, Vickers hardness, flexural strength, flexural modulus and volumetric shrinkage of experimental composite containing a low shrinkage monomer FIT-852 (FIT; ...
Laser Processing of Ni-Based Superalloy Surfaces Susceptible to Stress Concentration
(MDPI, Basel, 2021)
Reliable and resilient constructions are basic for ensuring the safety of various structures. The superalloys are used as constructive materials due to their superb mechanical properties and endurance. However, even these ...
Butt welded joints assessment after fire exposure
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The need of in service life of a steel structure after being exposed to fire raises the problem of strengthening or replacement of some structural elements. In many cases, after structural safety assessment, fire exposed ...
Numerical and Experimental Investigations of Fracture Behaviour of Welded Joints with Multiple Defects
(MDPI, Basel, 2021)
Current standards related to welded joint defects (EN ISO 5817) only consider individual cases (i.e., single defect in a welded joint). The question remains about the behaviour of a welded joint in the simultaneous presence ...
Welded joint geometry effect on fatigue crack growth resistance in different metallic materials
(Elsevier Sci Ltd, Oxford, 2021)
Fatigue crack growth through different welded joint regions was investigated, in terms of welded joint geometry and fatigue crack position. In the first phase of investigation, numerical simulation of crack growth in a ...