TY  - JOUR
AU  - Nikolić, Maria Vesna
AU  - Vasiljević, Zorka Ž.
AU  - Luković, Miloljub D.
AU  - Pavlović, Vera P.
AU  - Krstić, Jugoslav B.
AU  - Vujančević, Jelena
AU  - Tadić, Nenad
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - https://machinery.mas.bg.ac.rs/handle/123456789/4066
AB  - Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), X‐ray diffraction (XRD), X‐ray photoelectron spectroscopy (XPS) and Raman spectroscopy confirmed the formation of nanocrystalline zinc‐ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy (SEM) and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30‐90% in the frequency range 42 Hz – 1 MHz at room temperature (25 °C) and 50 °C. At 42 Hz at both analyzed temperatures the impedance reduced ~ 46 times in the humidity range 30‐90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.
PB  - Wiley
T2  - International Journal of Applied Ceramic Technology
T1  - Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing
EP  - 993
IS  - 3
SP  - 981
VL  - 16
DO  - 10.1111/ijac.13190
ER  - 

@article{
author = "Nikolić, Maria Vesna and Vasiljević, Zorka Ž. and Luković, Miloljub D. and Pavlović, Vera P. and Krstić, Jugoslav B. and Vujančević, Jelena and Tadić, Nenad and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2019",
abstract = "Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), X‐ray diffraction (XRD), X‐ray photoelectron spectroscopy (XPS) and Raman spectroscopy confirmed the formation of nanocrystalline zinc‐ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy (SEM) and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30‐90% in the frequency range 42 Hz – 1 MHz at room temperature (25 °C) and 50 °C. At 42 Hz at both analyzed temperatures the impedance reduced ~ 46 times in the humidity range 30‐90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.",
publisher = "Wiley",
journal = "International Journal of Applied Ceramic Technology",
title = "Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing",
pages = "993-981",
number = "3",
volume = "16",
doi = "10.1111/ijac.13190"
}

Nikolić, M. V., Vasiljević, Z. Ž., Luković, M. D., Pavlović, V. P., Krstić, J. B., Vujančević, J., Tadić, N., Vlahović, B.,& Pavlović, V. B.. (2019). Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing. in International Journal of Applied Ceramic Technology
Wiley., 16(3), 981-993.
https://doi.org/10.1111/ijac.13190

Nikolić MV, Vasiljević ZŽ, Luković MD, Pavlović VP, Krstić JB, Vujančević J, Tadić N, Vlahović B, Pavlović VB. Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing. in International Journal of Applied Ceramic Technology. 2019;16(3):981-993.
doi:10.1111/ijac.13190 .

Nikolić, Maria Vesna, Vasiljević, Zorka Ž., Luković, Miloljub D., Pavlović, Vera P., Krstić, Jugoslav B., Vujančević, Jelena, Tadić, Nenad, Vlahović, Branislav, Pavlović, Vladimir B., "Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing" in International Journal of Applied Ceramic Technology, 16, no. 3 (2019):981-993,
https://doi.org/10.1111/ijac.13190 . .

TY  - JOUR
AU  - Nikolić, Maria Vesna
AU  - Vasiljević, Zorka Ž.
AU  - Luković, Miloljub D.
AU  - Pavlović, Vera P.
AU  - Krstić, Jugoslav B.
AU  - Vujančević, Jelena
AU  - Tadić, Nenad
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - https://machinery.mas.bg.ac.rs/handle/123456789/3101
AB  - Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy and transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Raman spectroscopy confirmed the formation of nanocrystalline zinc-ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30%-90% in the frequency range 42 Hz-1 MHz at room temperature (25 degrees C) and 50 degrees C. At 42 Hz at both analyzed temperatures the impedance reduced 46 times in the humidity range 30%-90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.
PB  - Wiley, Hoboken
T2  - International Journal of Applied Ceramic Technology
T1  - Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing
EP  - 993
IS  - 3
SP  - 981
VL  - 16
DO  - 10.1111/ijac.13190
ER  - 

@article{
author = "Nikolić, Maria Vesna and Vasiljević, Zorka Ž. and Luković, Miloljub D. and Pavlović, Vera P. and Krstić, Jugoslav B. and Vujančević, Jelena and Tadić, Nenad and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2019",
abstract = "Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy and transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Raman spectroscopy confirmed the formation of nanocrystalline zinc-ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30%-90% in the frequency range 42 Hz-1 MHz at room temperature (25 degrees C) and 50 degrees C. At 42 Hz at both analyzed temperatures the impedance reduced 46 times in the humidity range 30%-90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.",
publisher = "Wiley, Hoboken",
journal = "International Journal of Applied Ceramic Technology",
title = "Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing",
pages = "993-981",
number = "3",
volume = "16",
doi = "10.1111/ijac.13190"
}

Nikolić, M. V., Vasiljević, Z. Ž., Luković, M. D., Pavlović, V. P., Krstić, J. B., Vujančević, J., Tadić, N., Vlahović, B.,& Pavlović, V. B.. (2019). Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing. in International Journal of Applied Ceramic Technology
Wiley, Hoboken., 16(3), 981-993.
https://doi.org/10.1111/ijac.13190

Nikolić MV, Vasiljević ZŽ, Luković MD, Pavlović VP, Krstić JB, Vujančević J, Tadić N, Vlahović B, Pavlović VB. Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing. in International Journal of Applied Ceramic Technology. 2019;16(3):981-993.
doi:10.1111/ijac.13190 .

Nikolić, Maria Vesna, Vasiljević, Zorka Ž., Luković, Miloljub D., Pavlović, Vera P., Krstić, Jugoslav B., Vujančević, Jelena, Tadić, Nenad, Vlahović, Branislav, Pavlović, Vladimir B., "Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen-printed thick films for application in humidity sensing" in International Journal of Applied Ceramic Technology, 16, no. 3 (2019):981-993,
https://doi.org/10.1111/ijac.13190 . .

TY  - JOUR
AU  - Nikolić, Maria Vesna
AU  - Vasiljević, Zorka Ž.
AU  - Luković, Miloljub D.
AU  - Pavlović, Vera P.
AU  - Vujančević, Jelena
AU  - Radovanović, Milan
AU  - Krstić, Jugoslav B.
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2018
UR  - https://machinery.mas.bg.ac.rs/handle/123456789/3945
AB  - Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (alpha-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 degrees C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz-1 MHz with humidity was analyzed at room temperature (25 degrees C) and 50 degrees C in the relative humidity range 30-90% and 40-90%, respectively. At 42 Hz, and room temperature the impedance reduced similar to 28 times, while at 50 degrees C it reduced similar to 147 times in the relative humidity range 40-90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 degrees C and 2.64% at 50 degrees C) showing that this is a promising material for application in humidity sensing.
PB  - Elsevier Science Sa, Lausanne
T2  - Sensors and Actuators B-Chemical
T1  - Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films
EP  - 664
SP  - 654
VL  - 277
DO  - 10.1016/j.snb.2018.09.063
ER  - 

@article{
author = "Nikolić, Maria Vesna and Vasiljević, Zorka Ž. and Luković, Miloljub D. and Pavlović, Vera P. and Vujančević, Jelena and Radovanović, Milan and Krstić, Jugoslav B. and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2018",
abstract = "Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (alpha-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 degrees C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz-1 MHz with humidity was analyzed at room temperature (25 degrees C) and 50 degrees C in the relative humidity range 30-90% and 40-90%, respectively. At 42 Hz, and room temperature the impedance reduced similar to 28 times, while at 50 degrees C it reduced similar to 147 times in the relative humidity range 40-90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 degrees C and 2.64% at 50 degrees C) showing that this is a promising material for application in humidity sensing.",
publisher = "Elsevier Science Sa, Lausanne",
journal = "Sensors and Actuators B-Chemical",
title = "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films",
pages = "664-654",
volume = "277",
doi = "10.1016/j.snb.2018.09.063"
}

Nikolić, M. V., Vasiljević, Z. Ž., Luković, M. D., Pavlović, V. P., Vujančević, J., Radovanović, M., Krstić, J. B., Vlahović, B.,& Pavlović, V. B.. (2018). Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B-Chemical
Elsevier Science Sa, Lausanne., 277, 654-664.
https://doi.org/10.1016/j.snb.2018.09.063

Nikolić MV, Vasiljević ZŽ, Luković MD, Pavlović VP, Vujančević J, Radovanović M, Krstić JB, Vlahović B, Pavlović VB. Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B-Chemical. 2018;277:654-664.
doi:10.1016/j.snb.2018.09.063 .

Nikolić, Maria Vesna, Vasiljević, Zorka Ž., Luković, Miloljub D., Pavlović, Vera P., Vujančević, Jelena, Radovanović, Milan, Krstić, Jugoslav B., Vlahović, Branislav, Pavlović, Vladimir B., "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films" in Sensors and Actuators B-Chemical, 277 (2018):654-664,
https://doi.org/10.1016/j.snb.2018.09.063 . .

TY  - JOUR
AU  - Nikolić, Maria Vesna
AU  - Vasiljević, Zorka Ž.
AU  - Luković, Miloljub D.
AU  - Pavlović, Vera P.
AU  - Vujančević, Jelena
AU  - Radovanović, Milan
AU  - Krstić, Jugoslav B.
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2018
UR  - https://machinery.mas.bg.ac.rs/handle/123456789/2887
AB  - Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (alpha-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 degrees C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz-1 MHz with humidity was analyzed at room temperature (25 degrees C) and 50 degrees C in the relative humidity range 30-90% and 40-90%, respectively. At 42 Hz, and room temperature the impedance reduced similar to 28 times, while at 50 degrees C it reduced similar to 147 times in the relative humidity range 40-90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 degrees C and 2.64% at 50 degrees C) showing that this is a promising material for application in humidity sensing.
PB  - Elsevier Science Sa, Lausanne
T2  - Sensors and Actuators B-Chemical
T1  - Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films
EP  - 664
SP  - 654
VL  - 277
DO  - 10.1016/j.snb.2018.09.063
ER  - 

@article{
author = "Nikolić, Maria Vesna and Vasiljević, Zorka Ž. and Luković, Miloljub D. and Pavlović, Vera P. and Vujančević, Jelena and Radovanović, Milan and Krstić, Jugoslav B. and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2018",
abstract = "Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (alpha-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 degrees C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz-1 MHz with humidity was analyzed at room temperature (25 degrees C) and 50 degrees C in the relative humidity range 30-90% and 40-90%, respectively. At 42 Hz, and room temperature the impedance reduced similar to 28 times, while at 50 degrees C it reduced similar to 147 times in the relative humidity range 40-90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 degrees C and 2.64% at 50 degrees C) showing that this is a promising material for application in humidity sensing.",
publisher = "Elsevier Science Sa, Lausanne",
journal = "Sensors and Actuators B-Chemical",
title = "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films",
pages = "664-654",
volume = "277",
doi = "10.1016/j.snb.2018.09.063"
}

Nikolić, M. V., Vasiljević, Z. Ž., Luković, M. D., Pavlović, V. P., Vujančević, J., Radovanović, M., Krstić, J. B., Vlahović, B.,& Pavlović, V. B.. (2018). Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B-Chemical
Elsevier Science Sa, Lausanne., 277, 654-664.
https://doi.org/10.1016/j.snb.2018.09.063

Nikolić MV, Vasiljević ZŽ, Luković MD, Pavlović VP, Vujančević J, Radovanović M, Krstić JB, Vlahović B, Pavlović VB. Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B-Chemical. 2018;277:654-664.
doi:10.1016/j.snb.2018.09.063 .

Nikolić, Maria Vesna, Vasiljević, Zorka Ž., Luković, Miloljub D., Pavlović, Vera P., Vujančević, Jelena, Radovanović, Milan, Krstić, Jugoslav B., Vlahović, Branislav, Pavlović, Vladimir B., "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films" in Sensors and Actuators B-Chemical, 277 (2018):654-664,
https://doi.org/10.1016/j.snb.2018.09.063 . .