The subject of this paper is investigation of the damage level of API J55 steel, used for manufacturing casing pipes by high frequency (HF) contact welding. The analysed pipe was withdrawn after about 70 000 hours of service in an oil drilling rig. Experimental analysis included determining the mechanical properties of the base material and welded joint, in particular the tensile and impact toughness testing. Fracture behaviour is examined by testing the modified compact tension (CT) specimens machined with a pre-crack in the base metal, weld metal and heat affected zone (HAZ). The critical value of the stress intensity factor K(Ic) is determined using the critical value of the J integral J(Ic). Fatigue crack growth rate and fatigue threshold stress intensity factor range are determined by three point bending tests of the Charpy specimens with a V-notch. The investigation conducted on specimens cut from the exploited pipe and the new pipe of the same grade revealed that material proper...ties were not seriously altered during the analysed period of service.
Ključne reči:
Pipe integrity / High frequency contact welaing / Damage level / Casing pipeIzvor:
Strojarstvo, 2009, 51, 4, 303-311Izdavač:
- Croation Union of Mech. Engineers and Naval Architects
Finansiranje / projekti:
- Specijalne teme mehanike loma materijala (RS-MESTD-MPN2006-2010-144027)
- Istraživanje i razvoj metoda za ocenu integriteta i pouzdanosti zavarenih cevi u naftnoj industriji (RS-MESTD-MPN2006-2010-14014)
Institucija/grupa
Inovacioni centarTY - JOUR AU - Šarkočević, Živče AU - Arsić, Miodrag AU - Međo, Bojan AU - Kozak, Dražan AU - Rakin, Marko AU - Burzić, Zijah AU - Sedmak, Aleksandar PY - 2009 UR - https://machinery.mas.bg.ac.rs/handle/123456789/868 AB - The subject of this paper is investigation of the damage level of API J55 steel, used for manufacturing casing pipes by high frequency (HF) contact welding. The analysed pipe was withdrawn after about 70 000 hours of service in an oil drilling rig. Experimental analysis included determining the mechanical properties of the base material and welded joint, in particular the tensile and impact toughness testing. Fracture behaviour is examined by testing the modified compact tension (CT) specimens machined with a pre-crack in the base metal, weld metal and heat affected zone (HAZ). The critical value of the stress intensity factor K(Ic) is determined using the critical value of the J integral J(Ic). Fatigue crack growth rate and fatigue threshold stress intensity factor range are determined by three point bending tests of the Charpy specimens with a V-notch. The investigation conducted on specimens cut from the exploited pipe and the new pipe of the same grade revealed that material properties were not seriously altered during the analysed period of service. PB - Croation Union of Mech. Engineers and Naval Architects T2 - Strojarstvo T1 - Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes EP - 311 IS - 4 SP - 303 VL - 51 UR - https://hdl.handle.net/21.15107/rcub_technorep_1360 ER -
@article{ author = "Šarkočević, Živče and Arsić, Miodrag and Međo, Bojan and Kozak, Dražan and Rakin, Marko and Burzić, Zijah and Sedmak, Aleksandar", year = "2009", abstract = "The subject of this paper is investigation of the damage level of API J55 steel, used for manufacturing casing pipes by high frequency (HF) contact welding. The analysed pipe was withdrawn after about 70 000 hours of service in an oil drilling rig. Experimental analysis included determining the mechanical properties of the base material and welded joint, in particular the tensile and impact toughness testing. Fracture behaviour is examined by testing the modified compact tension (CT) specimens machined with a pre-crack in the base metal, weld metal and heat affected zone (HAZ). The critical value of the stress intensity factor K(Ic) is determined using the critical value of the J integral J(Ic). Fatigue crack growth rate and fatigue threshold stress intensity factor range are determined by three point bending tests of the Charpy specimens with a V-notch. The investigation conducted on specimens cut from the exploited pipe and the new pipe of the same grade revealed that material properties were not seriously altered during the analysed period of service.", publisher = "Croation Union of Mech. Engineers and Naval Architects", journal = "Strojarstvo", title = "Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes", pages = "311-303", number = "4", volume = "51", url = "https://hdl.handle.net/21.15107/rcub_technorep_1360" }
Šarkočević, Ž., Arsić, M., Međo, B., Kozak, D., Rakin, M., Burzić, Z.,& Sedmak, A.. (2009). Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes. in Strojarstvo Croation Union of Mech. Engineers and Naval Architects., 51(4), 303-311. https://hdl.handle.net/21.15107/rcub_technorep_1360
Šarkočević Ž, Arsić M, Međo B, Kozak D, Rakin M, Burzić Z, Sedmak A. Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes. in Strojarstvo. 2009;51(4):303-311. https://hdl.handle.net/21.15107/rcub_technorep_1360 .
Šarkočević, Živče, Arsić, Miodrag, Međo, Bojan, Kozak, Dražan, Rakin, Marko, Burzić, Zijah, Sedmak, Aleksandar, "Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes" in Strojarstvo, 51, no. 4 (2009):303-311, https://hdl.handle.net/21.15107/rcub_technorep_1360 .