Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels
Апстракт
The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have somedifferent fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue andstress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, andemphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will bediscussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanningelectron microscopy will be presented in this paper.
Кључне речи:
Corrosion / fatigue / stress corrosion cracking / low alloy steelИзвор:
Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia, 2018, 129-Издавач:
- Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)
Колекције
Институција/група
Inovacioni centarTY - CONF AU - Momčilović, Dejan B. AU - Atanasovska, Ivana AU - Milović, Ljubica AU - Odanović, Zoran PY - 2018 UR - https://machinery.mas.bg.ac.rs/handle/123456789/7527 AB - The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have somedifferent fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue andstress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, andemphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will bediscussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanningelectron microscopy will be presented in this paper. PB - Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK) C3 - Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia T1 - Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels SP - 129 UR - https://hdl.handle.net/21.15107/rcub_machinery_7527 ER -
@conference{ author = "Momčilović, Dejan B. and Atanasovska, Ivana and Milović, Ljubica and Odanović, Zoran", year = "2018", abstract = "The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have somedifferent fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue andstress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, andemphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will bediscussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanningelectron microscopy will be presented in this paper.", publisher = "Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)", journal = "Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia", title = "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels", pages = "129", url = "https://hdl.handle.net/21.15107/rcub_machinery_7527" }
Momčilović, D. B., Atanasovska, I., Milović, L.,& Odanović, Z.. (2018). Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)., 129. https://hdl.handle.net/21.15107/rcub_machinery_7527
Momčilović DB, Atanasovska I, Milović L, Odanović Z. Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia. 2018;:129. https://hdl.handle.net/21.15107/rcub_machinery_7527 .
Momčilović, Dejan B., Atanasovska, Ivana, Milović, Ljubica, Odanović, Zoran, "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels" in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia (2018):129, https://hdl.handle.net/21.15107/rcub_machinery_7527 .