Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
2017
Аутори
Pavlović, MarkoDojčinović, Marina
Martinović, Sanja
Vlahović, Milica
Stević, Zoran
Jovanović, Marina
Volkov-Husović, Tatjana
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.
Кључне речи:
zircon based ceramic / cavitation erosion / mass loss / image analysis / thermal imagingИзвор:
Science of Sintering, 2017, 49Финансирање / пројекти:
- Имплементација савременијих техничко-технолошких и еколошких решења у постојећим производним системима Рудника Бакра Бор и Рудника Бакра Мајданпек (RS-MESTD-Technological Development (TD or TR)-33007)
- Синтеза, процесирање и карактеризација наноструктурних материјала за примену у области енергије, механичког инжењерства, заштите животне стредине и биомедицине (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Развој нових методологија ревитализације турбинске и хидромеханичке опреме хидроелектрана у зависности од узрока деградације материјала (RS-MESTD-Technological Development (TD or TR)-35002)
- Нов приступ дизајнирању материјала за конверзију и складиштење енергије (RS-MESTD-Basic Research (BR or ON)-172060)
Колекције
Институција/група
Inovacioni centarTY - JOUR AU - Pavlović, Marko AU - Dojčinović, Marina AU - Martinović, Sanja AU - Vlahović, Milica AU - Stević, Zoran AU - Jovanović, Marina AU - Volkov-Husović, Tatjana PY - 2017 UR - https://machinery.mas.bg.ac.rs/handle/123456789/7442 AB - Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected. T2 - Science of Sintering T1 - Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic VL - 49 DO - 10.2298/SOS1702175P ER -
@article{ author = "Pavlović, Marko and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Jovanović, Marina and Volkov-Husović, Tatjana", year = "2017", abstract = "Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.", journal = "Science of Sintering", title = "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic", volume = "49", doi = "10.2298/SOS1702175P" }
Pavlović, M., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z., Jovanović, M.,& Volkov-Husović, T.. (2017). Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering, 49. https://doi.org/10.2298/SOS1702175P
Pavlović M, Dojčinović M, Martinović S, Vlahović M, Stević Z, Jovanović M, Volkov-Husović T. Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering. 2017;49. doi:10.2298/SOS1702175P .
Pavlović, Marko, Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Jovanović, Marina, Volkov-Husović, Tatjana, "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic" in Science of Sintering, 49 (2017), https://doi.org/10.2298/SOS1702175P . .