Damage to a tube of output reheater due to gas corrosion
Аутори
Pavkov, VladimirBakić, Gordana
Maksimović, Vesna
Đukić, Miloš
Rajičić, Bratislav
Maslarević, Aleksandar
Matović, Branko
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
One of the most responsible elements of modern steam boilers are steam superheaters and reheaters.
These heating surfaces are inside the boiler chamber and consist of tubes connected to the inlet and
outlet header. Due to the complexity of service conditions, boiler tubes are exposed to processes of
gradual degradation, and consequently a decrease in operating performance and reliability.
In the operation of thermal power plants, irreversible metal losses resulting from corrosion can
cause tube failure and plant outage. Considering the loss of materials, gas corrosion in the dry gas
atmosphere due to the high temperature is of great importance. Gas corrosion can be expressed in
the boiler tubing system due to the presence of sulfur compounds in the flue gases. For this reason,
it must be borne in mind that the outer surface of a tube of final reheater has different damage
mechanisms during operation, and one of them is gas corrosion. Gas corrosion causes material loss
and pro...vides a site for crack initiation and propagation, which can compromise the integrity of the
pressure vessel.
In this paper, a tube of a final reheater from a 210 MW power plant was tested. The tube was in
service 200,000 h at a working temperature of 540 °C and a maximum working pressure of 4.6
MPa. The tube is made of low alloy Cr-Mo-V steel, class 12H1MF (GOST). After long-term
service, a rough surface and loss of the material in the form of a crater were observed on the outer
surface of the tube as a result of the effect of gas corrosion, together with the change of
microstructure due to elevated service temperature. The measured depth of damage to the tube is
120 m. The presence of gas corrosion on the tube was confirmed and measured by an optical
microscope, Figure 1.
Извор:
Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022, 2022Издавач:
- Belgrade : Vinča Institute of Nuclear Sciences - National Institute of thе Republic of Serbia, University of Belgrade
- Belgrade : Serbian Society for Innovative Materials in Extreme Conditions (SIM-EXTREME)
Колекције
Институција/група
Mašinski fakultetTY - CONF AU - Pavkov, Vladimir AU - Bakić, Gordana AU - Maksimović, Vesna AU - Đukić, Miloš AU - Rajičić, Bratislav AU - Maslarević, Aleksandar AU - Matović, Branko PY - 2022 UR - https://machinery.mas.bg.ac.rs/handle/123456789/7430 AB - One of the most responsible elements of modern steam boilers are steam superheaters and reheaters. These heating surfaces are inside the boiler chamber and consist of tubes connected to the inlet and outlet header. Due to the complexity of service conditions, boiler tubes are exposed to processes of gradual degradation, and consequently a decrease in operating performance and reliability. In the operation of thermal power plants, irreversible metal losses resulting from corrosion can cause tube failure and plant outage. Considering the loss of materials, gas corrosion in the dry gas atmosphere due to the high temperature is of great importance. Gas corrosion can be expressed in the boiler tubing system due to the presence of sulfur compounds in the flue gases. For this reason, it must be borne in mind that the outer surface of a tube of final reheater has different damage mechanisms during operation, and one of them is gas corrosion. Gas corrosion causes material loss and provides a site for crack initiation and propagation, which can compromise the integrity of the pressure vessel. In this paper, a tube of a final reheater from a 210 MW power plant was tested. The tube was in service 200,000 h at a working temperature of 540 °C and a maximum working pressure of 4.6 MPa. The tube is made of low alloy Cr-Mo-V steel, class 12H1MF (GOST). After long-term service, a rough surface and loss of the material in the form of a crater were observed on the outer surface of the tube as a result of the effect of gas corrosion, together with the change of microstructure due to elevated service temperature. The measured depth of damage to the tube is 120 m. The presence of gas corrosion on the tube was confirmed and measured by an optical microscope, Figure 1. PB - Belgrade : Vinča Institute of Nuclear Sciences - National Institute of thе Republic of Serbia, University of Belgrade PB - Belgrade : Serbian Society for Innovative Materials in Extreme Conditions (SIM-EXTREME) C3 - Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022 T1 - Damage to a tube of output reheater due to gas corrosion UR - https://hdl.handle.net/21.15107/rcub_machinery_7430 ER -
@conference{ author = "Pavkov, Vladimir and Bakić, Gordana and Maksimović, Vesna and Đukić, Miloš and Rajičić, Bratislav and Maslarević, Aleksandar and Matović, Branko", year = "2022", abstract = "One of the most responsible elements of modern steam boilers are steam superheaters and reheaters. These heating surfaces are inside the boiler chamber and consist of tubes connected to the inlet and outlet header. Due to the complexity of service conditions, boiler tubes are exposed to processes of gradual degradation, and consequently a decrease in operating performance and reliability. In the operation of thermal power plants, irreversible metal losses resulting from corrosion can cause tube failure and plant outage. Considering the loss of materials, gas corrosion in the dry gas atmosphere due to the high temperature is of great importance. Gas corrosion can be expressed in the boiler tubing system due to the presence of sulfur compounds in the flue gases. For this reason, it must be borne in mind that the outer surface of a tube of final reheater has different damage mechanisms during operation, and one of them is gas corrosion. Gas corrosion causes material loss and provides a site for crack initiation and propagation, which can compromise the integrity of the pressure vessel. In this paper, a tube of a final reheater from a 210 MW power plant was tested. The tube was in service 200,000 h at a working temperature of 540 °C and a maximum working pressure of 4.6 MPa. The tube is made of low alloy Cr-Mo-V steel, class 12H1MF (GOST). After long-term service, a rough surface and loss of the material in the form of a crater were observed on the outer surface of the tube as a result of the effect of gas corrosion, together with the change of microstructure due to elevated service temperature. The measured depth of damage to the tube is 120 m. The presence of gas corrosion on the tube was confirmed and measured by an optical microscope, Figure 1.", publisher = "Belgrade : Vinča Institute of Nuclear Sciences - National Institute of thе Republic of Serbia, University of Belgrade, Belgrade : Serbian Society for Innovative Materials in Extreme Conditions (SIM-EXTREME)", journal = "Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022", title = "Damage to a tube of output reheater due to gas corrosion", url = "https://hdl.handle.net/21.15107/rcub_machinery_7430" }
Pavkov, V., Bakić, G., Maksimović, V., Đukić, M., Rajičić, B., Maslarević, A.,& Matović, B.. (2022). Damage to a tube of output reheater due to gas corrosion. in Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022 Belgrade : Vinča Institute of Nuclear Sciences - National Institute of thе Republic of Serbia, University of Belgrade.. https://hdl.handle.net/21.15107/rcub_machinery_7430
Pavkov V, Bakić G, Maksimović V, Đukić M, Rajičić B, Maslarević A, Matović B. Damage to a tube of output reheater due to gas corrosion. in Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022. 2022;. https://hdl.handle.net/21.15107/rcub_machinery_7430 .
Pavkov, Vladimir, Bakić, Gordana, Maksimović, Vesna, Đukić, Miloš, Rajičić, Bratislav, Maslarević, Aleksandar, Matović, Branko, "Damage to a tube of output reheater due to gas corrosion" in Program and Book of abstracts of the 1st Intentational conference on innovativ materials in extreme conditions IMEC2022 (2022), https://hdl.handle.net/21.15107/rcub_machinery_7430 .