Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator
Нема приказа
Конференцијски прилог (Објављена верзија)
,
Trans Tech Publications Ltd, www.scientific.net
Метаподаци
Приказ свих података о документуАпстракт
This paper deals with damage analysis of gear ring after manufacturing process, just before in-service period. Tooth gear ring segments were made of 40MnCrSi3V low-alloyed cast steel, which chemical composition and mechanical properties were given in table 1 and 2, respectively. Concerning parent material characteristics, in this case low-alloyed cast steel 40 MnCrSi3V, inspection and control of gear segments were necessary to be performed after manufacturing. Non-destructive testing method with magnet particles (MT) of fluorescent suspension of particle size 3 µm was performed for potential defects detection. Surface indications were observed on 8 out of 12 gear segments on these new parts, where the lengths of the cracks goes up to 110 mm. Some of the observed defects were shown in Fig. 1. Defects were located in segments main body the gear teeth, its main body etc. Taking into account aforementioned, observed defects on new gear ring segments were caused in manufacturing process i.e.... by casting process and inadequate cooling rate.
Кључне речи:
Damage Analysis / Gear / Bucket-Wheel Excavator / Low-Alloyed Cast SteelИзвор:
Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary), 2023, 2, 67-Издавач:
- Trans Tech Publications Ltd, Switzerland
Финансирање / пројекти:
- 451-03-47/2023-01/200213
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200213 (Иновациони центар Машинског факултета у Београду доо) (RS-MESTD-inst-2020-200213)
URI
https://main.scientific.net/book/book-of-abstracts-from-9th-international-scientific-conference-on-advances-in-mechanical-engineering/978-3-0364-1445-4/ebookhttps://machinery.mas.bg.ac.rs/handle/123456789/7170
Колекције
Институција/група
Inovacioni centarTY - CONF AU - Miladinov, Milan AU - Sedmak, Simon AU - Đorđević, Branislav R. AU - Petrović, Ana AU - Vučetić, Filip PY - 2023 UR - https://main.scientific.net/book/book-of-abstracts-from-9th-international-scientific-conference-on-advances-in-mechanical-engineering/978-3-0364-1445-4/ebook UR - https://machinery.mas.bg.ac.rs/handle/123456789/7170 AB - This paper deals with damage analysis of gear ring after manufacturing process, just before in-service period. Tooth gear ring segments were made of 40MnCrSi3V low-alloyed cast steel, which chemical composition and mechanical properties were given in table 1 and 2, respectively. Concerning parent material characteristics, in this case low-alloyed cast steel 40 MnCrSi3V, inspection and control of gear segments were necessary to be performed after manufacturing. Non-destructive testing method with magnet particles (MT) of fluorescent suspension of particle size 3 µm was performed for potential defects detection. Surface indications were observed on 8 out of 12 gear segments on these new parts, where the lengths of the cracks goes up to 110 mm. Some of the observed defects were shown in Fig. 1. Defects were located in segments main body the gear teeth, its main body etc. Taking into account aforementioned, observed defects on new gear ring segments were caused in manufacturing process i.e. by casting process and inadequate cooling rate. PB - Trans Tech Publications Ltd, Switzerland C3 - Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary) T1 - Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator SP - 67 VL - 2 UR - https://hdl.handle.net/21.15107/rcub_machinery_7170 ER -
@conference{ author = "Miladinov, Milan and Sedmak, Simon and Đorđević, Branislav R. and Petrović, Ana and Vučetić, Filip", year = "2023", abstract = "This paper deals with damage analysis of gear ring after manufacturing process, just before in-service period. Tooth gear ring segments were made of 40MnCrSi3V low-alloyed cast steel, which chemical composition and mechanical properties were given in table 1 and 2, respectively. Concerning parent material characteristics, in this case low-alloyed cast steel 40 MnCrSi3V, inspection and control of gear segments were necessary to be performed after manufacturing. Non-destructive testing method with magnet particles (MT) of fluorescent suspension of particle size 3 µm was performed for potential defects detection. Surface indications were observed on 8 out of 12 gear segments on these new parts, where the lengths of the cracks goes up to 110 mm. Some of the observed defects were shown in Fig. 1. Defects were located in segments main body the gear teeth, its main body etc. Taking into account aforementioned, observed defects on new gear ring segments were caused in manufacturing process i.e. by casting process and inadequate cooling rate.", publisher = "Trans Tech Publications Ltd, Switzerland", journal = "Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary)", title = "Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator", pages = "67", volume = "2", url = "https://hdl.handle.net/21.15107/rcub_machinery_7170" }
Miladinov, M., Sedmak, S., Đorđević, B. R., Petrović, A.,& Vučetić, F.. (2023). Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator. in Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary) Trans Tech Publications Ltd, Switzerland., 2, 67. https://hdl.handle.net/21.15107/rcub_machinery_7170
Miladinov M, Sedmak S, Đorđević BR, Petrović A, Vučetić F. Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator. in Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary). 2023;2:67. https://hdl.handle.net/21.15107/rcub_machinery_7170 .
Miladinov, Milan, Sedmak, Simon, Đorđević, Branislav R., Petrović, Ana, Vučetić, Filip, "Damage Analysis on Tooth Gear Ring of a Bucket-Wheel Excavator" in Book of Abstracts from 9th International Scientific Conference on Advances in Mechanical Engineering (ISCAME, November 9-10, 2023, Debrecen, Hungary), 2 (2023):67, https://hdl.handle.net/21.15107/rcub_machinery_7170 .