The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment

Abstract

In this paper is presented the principle of application of fracture mechanics parameters in determining the integrity of rotary equipment. The behavior of rotary equipment depends on presence of cracks and basically determines the integrity and life of such equipment. The locations of stress concentration (i.e. radius changes) represent a particular problem in rotary equipment, and they are the most suitable places for the occurrence of microcracks i.e. cracks due to fatigue load. This problem is most common in the shaft of relatively large dimensions, for example, turbine shafts in hydropower plants made of high-strength carbon steel with relatively low fracture toughness, and relatively low resistance to crack formation and growth. Having in mind that rotary equipment represents the great risk in the exploitation, whose occasional failures often had severe consequences, it is necessary detail study of their integrity. For this purpose, it is necessary application of parameters of linear-elastic fracture mechanics, such as stress intensity factor, which range defines the rate of crack growth (Parisian law), and its critical value (fracture toughness) determines the critical crack length. The procedures for determining the critical crack length will be described using the fracture mechanics parameters.