The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment
Abstract
In this paper is presented the principle of application of fracture mechanics parameters in determining the integrity of rotary equipment. The behavior of rotary equipment depends on presence of cracks and basically determines the integrity and life of such equipment. The locations of stress concentration (i.e. radius changes) represent a particular problem in rotary equipment, and they are the most suitable places for the occurrence of microcracks i.e. cracks due to fatigue load. This problem is most common in the shaft of relatively large dimensions, for example, turbine shafts in hydropower plants made of high-strength carbon steel with relatively low fracture toughness, and relatively low resistance to crack formation and growth. Having in mind that rotary equipment represents the great risk in the exploitation, whose occasional failures often had severe consequences, it is necessary detail study of their integrity. For this purpose, it is necessary application of parameters of lin...ear-elastic fracture mechanics, such as stress intensity factor, which range defines the rate of crack growth (Parisian law), and its critical value (fracture toughness) determines the critical crack length. The procedures for determining the critical crack length will be described using the fracture mechanics parameters.
Keywords:
Fracture mechanic parameters / integrity assessment / rotary equipmentSource:
22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts, 2018, 97-URI
http://www.ecf22.rs/docs/Book%20of%20Abstracts%20ECF22.pdfhttps://machinery.mas.bg.ac.rs/handle/123456789/6246
Collections
Institution/Community
Inovacioni centarTY - CONF AU - Milovanović, Nikola AU - Bakić, Gordana AU - Đorđević, Branislav AU - Sedmak, Aleksandar PY - 2018 UR - http://www.ecf22.rs/docs/Book%20of%20Abstracts%20ECF22.pdf UR - https://machinery.mas.bg.ac.rs/handle/123456789/6246 AB - In this paper is presented the principle of application of fracture mechanics parameters in determining the integrity of rotary equipment. The behavior of rotary equipment depends on presence of cracks and basically determines the integrity and life of such equipment. The locations of stress concentration (i.e. radius changes) represent a particular problem in rotary equipment, and they are the most suitable places for the occurrence of microcracks i.e. cracks due to fatigue load. This problem is most common in the shaft of relatively large dimensions, for example, turbine shafts in hydropower plants made of high-strength carbon steel with relatively low fracture toughness, and relatively low resistance to crack formation and growth. Having in mind that rotary equipment represents the great risk in the exploitation, whose occasional failures often had severe consequences, it is necessary detail study of their integrity. For this purpose, it is necessary application of parameters of linear-elastic fracture mechanics, such as stress intensity factor, which range defines the rate of crack growth (Parisian law), and its critical value (fracture toughness) determines the critical crack length. The procedures for determining the critical crack length will be described using the fracture mechanics parameters. C3 - 22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts T1 - The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment SP - 97 UR - https://hdl.handle.net/21.15107/rcub_machinery_6246 ER -
@conference{ author = "Milovanović, Nikola and Bakić, Gordana and Đorđević, Branislav and Sedmak, Aleksandar", year = "2018", abstract = "In this paper is presented the principle of application of fracture mechanics parameters in determining the integrity of rotary equipment. The behavior of rotary equipment depends on presence of cracks and basically determines the integrity and life of such equipment. The locations of stress concentration (i.e. radius changes) represent a particular problem in rotary equipment, and they are the most suitable places for the occurrence of microcracks i.e. cracks due to fatigue load. This problem is most common in the shaft of relatively large dimensions, for example, turbine shafts in hydropower plants made of high-strength carbon steel with relatively low fracture toughness, and relatively low resistance to crack formation and growth. Having in mind that rotary equipment represents the great risk in the exploitation, whose occasional failures often had severe consequences, it is necessary detail study of their integrity. For this purpose, it is necessary application of parameters of linear-elastic fracture mechanics, such as stress intensity factor, which range defines the rate of crack growth (Parisian law), and its critical value (fracture toughness) determines the critical crack length. The procedures for determining the critical crack length will be described using the fracture mechanics parameters.", journal = "22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts", title = "The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment", pages = "97", url = "https://hdl.handle.net/21.15107/rcub_machinery_6246" }
Milovanović, N., Bakić, G., Đorđević, B.,& Sedmak, A.. (2018). The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment. in 22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts, 97. https://hdl.handle.net/21.15107/rcub_machinery_6246
Milovanović N, Bakić G, Đorđević B, Sedmak A. The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment. in 22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts. 2018;:97. https://hdl.handle.net/21.15107/rcub_machinery_6246 .
Milovanović, Nikola, Bakić, Gordana, Đorđević, Branislav, Sedmak, Aleksandar, "The influence of oxide deposits on the remaining life and integrity of pressure vessels equipment" in 22nd European Conference on Fracture - ECF22 LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY Book of Abstracts (2018):97, https://hdl.handle.net/21.15107/rcub_machinery_6246 .