The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics
2021
Аутори
Živojinović, JelenaBlagojević, Vladimir A.
Pavlović, Vera P.
Kosanović, Darko
Tadić, Nenad
Pavlović, Vladimir B.
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In recent years, a lot of interest has been shown in obtaining materials with predetermined properties. The aim is to establish a functional dependence between the synthesis parameters, structural characteristics, and properties of the material. Ceramic materials based on strontium titanate (SrTiO3) are of special interest due to their unique physical-chemical properties. Having in mind the importance of examining the influence of synthesis parameters on the process of obtaining and properties of functional electroceramic materials, and the importance of SrTiO3 as a perovskite material, the motive was to analyze and consider the influence of mechanical activation. It has been established that the time of mechanical activation (0, 10, 30, 60, 90, and 120 minutes) of SrTiO3 powders indirectly affects on electrical properties of SrTiO3 ceramics. It was noticed that in SrTiO3 ceramics the values of relative dielectric permittivity in the radio frequency range (0,3 MHz - 3 GHz) are stable, ...which is important for the fabrication of electronic components. Microstructural SEM analysis showed that the increase in mechanical activation time results in less porous samples. It was found that the value of the relative dielectric permittivity of ceramic samples at room temperature changes following the combined effect of changes in sample density, grain size, as well as changes in the grain boundary region. The maximum value of dielectric permittivity was observed in the sample activated for 10 minutes. Also, the sample activated for 10 min exhibits relatively low values of loss tangent, compared to the other mechanically activated samples, providing the best overall dielectric performance compared to other samples.
Кључне речи:
strontium titanate / mechanical activation / sintering / electrical propertiesИзвор:
Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia, 2021Издавач:
- Innovation Center of Faculty of Mechanical Engineering, Belgrade
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200175 (Институт техничких наука САНУ, Београд) (RS-MESTD-inst-2020-200175)
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200105 (Универзитет у Београду, Машински факултет) (RS-MESTD-inst-2020-200105)
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200116 (Универзитет у Београду, Пољопривредни факултет) (RS-MESTD-inst-2020-200116)
Колекције
Институција/група
Mašinski fakultetTY - CONF AU - Živojinović, Jelena AU - Blagojević, Vladimir A. AU - Pavlović, Vera P. AU - Kosanović, Darko AU - Tadić, Nenad AU - Pavlović, Vladimir B. PY - 2021 UR - https://machinery.mas.bg.ac.rs/handle/123456789/4224 AB - In recent years, a lot of interest has been shown in obtaining materials with predetermined properties. The aim is to establish a functional dependence between the synthesis parameters, structural characteristics, and properties of the material. Ceramic materials based on strontium titanate (SrTiO3) are of special interest due to their unique physical-chemical properties. Having in mind the importance of examining the influence of synthesis parameters on the process of obtaining and properties of functional electroceramic materials, and the importance of SrTiO3 as a perovskite material, the motive was to analyze and consider the influence of mechanical activation. It has been established that the time of mechanical activation (0, 10, 30, 60, 90, and 120 minutes) of SrTiO3 powders indirectly affects on electrical properties of SrTiO3 ceramics. It was noticed that in SrTiO3 ceramics the values of relative dielectric permittivity in the radio frequency range (0,3 MHz - 3 GHz) are stable, which is important for the fabrication of electronic components. Microstructural SEM analysis showed that the increase in mechanical activation time results in less porous samples. It was found that the value of the relative dielectric permittivity of ceramic samples at room temperature changes following the combined effect of changes in sample density, grain size, as well as changes in the grain boundary region. The maximum value of dielectric permittivity was observed in the sample activated for 10 minutes. Also, the sample activated for 10 min exhibits relatively low values of loss tangent, compared to the other mechanically activated samples, providing the best overall dielectric performance compared to other samples. PB - Innovation Center of Faculty of Mechanical Engineering, Belgrade C3 - Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia T1 - The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics UR - https://hdl.handle.net/21.15107/rcub_machinery_4224 ER -
@conference{ author = "Živojinović, Jelena and Blagojević, Vladimir A. and Pavlović, Vera P. and Kosanović, Darko and Tadić, Nenad and Pavlović, Vladimir B.", year = "2021", abstract = "In recent years, a lot of interest has been shown in obtaining materials with predetermined properties. The aim is to establish a functional dependence between the synthesis parameters, structural characteristics, and properties of the material. Ceramic materials based on strontium titanate (SrTiO3) are of special interest due to their unique physical-chemical properties. Having in mind the importance of examining the influence of synthesis parameters on the process of obtaining and properties of functional electroceramic materials, and the importance of SrTiO3 as a perovskite material, the motive was to analyze and consider the influence of mechanical activation. It has been established that the time of mechanical activation (0, 10, 30, 60, 90, and 120 minutes) of SrTiO3 powders indirectly affects on electrical properties of SrTiO3 ceramics. It was noticed that in SrTiO3 ceramics the values of relative dielectric permittivity in the radio frequency range (0,3 MHz - 3 GHz) are stable, which is important for the fabrication of electronic components. Microstructural SEM analysis showed that the increase in mechanical activation time results in less porous samples. It was found that the value of the relative dielectric permittivity of ceramic samples at room temperature changes following the combined effect of changes in sample density, grain size, as well as changes in the grain boundary region. The maximum value of dielectric permittivity was observed in the sample activated for 10 minutes. Also, the sample activated for 10 min exhibits relatively low values of loss tangent, compared to the other mechanically activated samples, providing the best overall dielectric performance compared to other samples.", publisher = "Innovation Center of Faculty of Mechanical Engineering, Belgrade", journal = "Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia", title = "The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics", url = "https://hdl.handle.net/21.15107/rcub_machinery_4224" }
Živojinović, J., Blagojević, V. A., Pavlović, V. P., Kosanović, D., Tadić, N.,& Pavlović, V. B.. (2021). The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics. in Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia Innovation Center of Faculty of Mechanical Engineering, Belgrade.. https://hdl.handle.net/21.15107/rcub_machinery_4224
Živojinović J, Blagojević VA, Pavlović VP, Kosanović D, Tadić N, Pavlović VB. The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics. in Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia. 2021;. https://hdl.handle.net/21.15107/rcub_machinery_4224 .
Živojinović, Jelena, Blagojević, Vladimir A., Pavlović, Vera P., Kosanović, Darko, Tadić, Nenad, Pavlović, Vladimir B., "The influence of mechanical activation on microstructure and dielectric properties of SrTiO3 ceramics" in Programme and The Book of Abstracts - International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2021, 29 June - 02 July 2021, Zlatibor, Serbia (2021), https://hdl.handle.net/21.15107/rcub_machinery_4224 .