Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping
2019
Аутори
Vujančević, JelenaAndričević, Pavao
Bjelajac, Andjelika
Đokić, Veljko
Popović, Maja
Rakocević, Zlatko
Horvath, Endre
Kollar, Marton
Nafradi, Balint
Schiller, Andreas
Domanski, Konrad
Forro, Laszlo
Pavlović, Vera P.
Janaćković, Đorđe
Чланак у часопису (Рецензирана верзија)
Метаподаци
Приказ свих података о документуАпстракт
Highly ordered, anodically grown TiO2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO2/CH3 NH3PbI3 single crystals. The N-TiO2/perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels o...f halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures.
Кључне речи:
Annealing in NH3 / Titanium dioxide nanotubes / Methylammonium lead triiodide photodetectors / Optical properties / PhotocurrentИзвор:
Ceramics International, 2019, 45, 8, 10013-10020Издавач:
- Elsevier
Финансирање / пројекти:
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-MESTD-Basic Research (BR or ON)-172057)
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45019)
- Swiss National Science Foundation [160169]
- ERC advanced grant "PICOPROP" [670918]
Напомена:
- This is the peer reviewed version of the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045
Повезане информације:
- Друга верзија
https://doi.org/10.1016/j.ceramint.2019.02.045 - Друга верзија
https://machinery.mas.bg.ac.rs/handle/123456789/3103
DOI: 10.1016/j.ceramint.2019.02.045
ISSN: 0272-8842
WoS: 000465058500040
Scopus: 2-s2.0-85061828876
Колекције
Институција/група
Mašinski fakultetTY - JOUR AU - Vujančević, Jelena AU - Andričević, Pavao AU - Bjelajac, Andjelika AU - Đokić, Veljko AU - Popović, Maja AU - Rakocević, Zlatko AU - Horvath, Endre AU - Kollar, Marton AU - Nafradi, Balint AU - Schiller, Andreas AU - Domanski, Konrad AU - Forro, Laszlo AU - Pavlović, Vera P. AU - Janaćković, Đorđe PY - 2019 UR - https://machinery.mas.bg.ac.rs/handle/123456789/4043 AB - Highly ordered, anodically grown TiO2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO2/CH3 NH3PbI3 single crystals. The N-TiO2/perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures. PB - Elsevier T2 - Ceramics International T1 - Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping EP - 10020 IS - 8 SP - 10013 VL - 45 DO - 10.1016/j.ceramint.2019.02.045 ER -
@article{ author = "Vujančević, Jelena and Andričević, Pavao and Bjelajac, Andjelika and Đokić, Veljko and Popović, Maja and Rakocević, Zlatko and Horvath, Endre and Kollar, Marton and Nafradi, Balint and Schiller, Andreas and Domanski, Konrad and Forro, Laszlo and Pavlović, Vera P. and Janaćković, Đorđe", year = "2019", abstract = "Highly ordered, anodically grown TiO2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO2/CH3 NH3PbI3 single crystals. The N-TiO2/perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures.", publisher = "Elsevier", journal = "Ceramics International", title = "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping", pages = "10020-10013", number = "8", volume = "45", doi = "10.1016/j.ceramint.2019.02.045" }
Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakocević, Z., Horvath, E., Kollar, M., Nafradi, B., Schiller, A., Domanski, K., Forro, L., Pavlović, V. P.,& Janaćković, Đ.. (2019). Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International Elsevier., 45(8), 10013-10020. https://doi.org/10.1016/j.ceramint.2019.02.045
Vujančević J, Andričević P, Bjelajac A, Đokić V, Popović M, Rakocević Z, Horvath E, Kollar M, Nafradi B, Schiller A, Domanski K, Forro L, Pavlović VP, Janaćković Đ. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International. 2019;45(8):10013-10020. doi:10.1016/j.ceramint.2019.02.045 .
Vujančević, Jelena, Andričević, Pavao, Bjelajac, Andjelika, Đokić, Veljko, Popović, Maja, Rakocević, Zlatko, Horvath, Endre, Kollar, Marton, Nafradi, Balint, Schiller, Andreas, Domanski, Konrad, Forro, Laszlo, Pavlović, Vera P., Janaćković, Đorđe, "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping" in Ceramics International, 45, no. 8 (2019):10013-10020, https://doi.org/10.1016/j.ceramint.2019.02.045 . .