Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...
XFEM based analysis of fatigue crack growth in damaged wing-uselage attachment lug
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
The research presented in this paper is based on the use of extended finite element method (XFEM) for stress intensity factors (SIFs) determination in the case of fatigue crack presented in the wing-fuselage attachment lug ...
Structural integrity and life assessment of rotating equipment
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
Failures of rotating equipment often cause severe consequences, so it is necessary to study their integrity and life as detailed as possible, especially when crack is detected. In the case studied here, hydro power plant ...
Influence of welded joint microstructures on fatigue behaviour of specimens with a notch in the heat affected zone
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, the results of determining the Paris law coefficients, C and m, are presented, based on the experimental data obtained by three-point bending testing of 8 welded joint specimens. The specimens were taken ...
Fracture mechanics and fatigue crack propagation in armor steel welds
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The welding process of armor steel is a complex process due to possible welding faults appearing in all zones of weld metal joint in the form of cracks and pores, as results of high percentage of carbon in the base metal. ...
Effect of material heterogeneity and testing temperature on fatigue behaviour of Cr-Mo steel welded joints
(Elsevier Ltd, 2022)
Successful application of Cr-Mo steel depends crucially on behaviour of all zones in welded joints, i.e. base metal (BM), heat-affected-zone (HAZ) and weld metal (WM), both at room and working temperature. Different amplitude ...