Integrity assessment and determination of residual fatigue life of vital parts of bucket-wheel excavator operating under dynamic loads
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper are presented results of tests and analyses of complex dynamic loads carried out on the bucket-wheel excavator SchRs 650/5x24 Krupp, as well as assessment of service life of vital welded structures of a ...
Fracture mechanics and fatigue crack propagation in armor steel welds
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The welding process of armor steel is a complex process due to possible welding faults appearing in all zones of weld metal joint in the form of cracks and pores, as results of high percentage of carbon in the base metal. ...
Influence of welded joint microstructures on fatigue behaviour of specimens with a notch in the heat affected zone
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, the results of determining the Paris law coefficients, C and m, are presented, based on the experimental data obtained by three-point bending testing of 8 welded joint specimens. The specimens were taken ...
The renewed TC12/ESIS technical committee - Risk analysis and safety of large structures and components
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The ESIS Executive Committee decided to nominate a new team for the leadership and management of the TC12/ESIS technical committee (TC), as well as update the TC name as "Risk Analysis and Safety of Large Structures and ...
Fatigue crack growth in a structure exposed to high temperature
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
The exhaust nozzle, made of titanium, is the part of a jet engine where the final expansion of the hot gas from the turbine occurs and where the speed of the exhaust gas is further increased to create thrust. During the ...
Butt welded joints assessment after fire exposure
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The need of in service life of a steel structure after being exposed to fire raises the problem of strengthening or replacement of some structural elements. In many cases, after structural safety assessment, fire exposed ...
Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...
Stress intensity factors numerical calculations for two penny shaped cracks in the elastic solid
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
In the face of enormous costs of developing new aircraft, high fuel prices, increasingly demanding environmental standards, harsh economic race and the fight against competing manufacturers, today's aviation is adapting ...
Engineering critical assessment of steel shell structure elements welded joints under high cycle fatigue
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
Existing flaws in critical parts of structural elements may lead to failures of subassemblies and, in case of lack of redundancy, even to the entire structure collapse. Considering the case of cyclic loading - wind load ...
Risk assessment of oil drilling rig welded pipe based on structural integrity and life estimation
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
Risk assessment procedure based on structural integrity and life estimation has been introduced and applied to oil drilling rig welded pipe. The new concept based on application of structural integrity and life estimation ...