Experimental investigations of flow distribution in coolant system of Helium-Cooled-Pebble-Bed Test Blanket Module
(Elsevier Science Sa, Lausanne, 2016)
This paper deals with investigations of flow distribution in the coolant system of the Helium-Cooled Pebble -Bed Test Blanket Module (HCPB TBM) for ITER. The investigations have been performed by manufacturing and testing ...
Numerical analysis of fatigue crack growth of hip implant
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Fatigue crack growth in hip implant has been analysed using the extended finite element method. Toward this aim, the three-dimensional finite element model is created and used in ABAQUS and Morfeo/crack add-in for ABAQUS ...
Effects of a low-Shrinkage methacrylate monomer and monoacylphosphine oxide photoinitiator on curing efficiency and mechanical properties of experimental resin-based composites
(Elsevier, Amsterdam, 2016)
This study investigated the degree of conversion, depth of cure, Vickers hardness, flexural strength, flexural modulus and volumetric shrinkage of experimental composite containing a low shrinkage monomer FIT-852 (FIT; ...
Determination of optimum wing spar cross section for maximum fatigue life
(Elsevier Sci Ltd, Oxford, 2019)
Shape optimisation is a nowadays-standard requirement in the design of lightweight structural components. In this paper, optimisation of I-beam cross-section of integral aluminium 2024-T3 wing spar is presented, taking the ...
Butt welded joints assessment after fire exposure
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The need of in service life of a steel structure after being exposed to fire raises the problem of strengthening or replacement of some structural elements. In many cases, after structural safety assessment, fire exposed ...
Effect of laser beam welded reinforcement on integral skin panel fatigue life
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, numerical analyses of fatigue crack growth in integral skin-stringer panel produced by means of laser beam welding (LBW) are presented along with fatigue results verified by previously conducted experiments. ...
Fatigue crack growth in a structure exposed to high temperature
(Pergamon-Elsevier Science Ltd, Oxford, 2021)
The exhaust nozzle, made of titanium, is the part of a jet engine where the final expansion of the hot gas from the turbine occurs and where the speed of the exhaust gas is further increased to create thrust. During the ...
Thermal-hydraulics of helium cooled First Wall channels and scoping investigations on performance improvement by application of ribs and mixing devices
(Elsevier Science Sa, Lausanne, 2016)
The first wall (FW) of DEMO is a component with high thermal loads. The cooling of the FW has to comply with the material's upper and lower temperature limits and requirements from stress assessment, like low temperature ...
Fracture mechanics and fatigue crack propagation in armor steel welds
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The welding process of armor steel is a complex process due to possible welding faults appearing in all zones of weld metal joint in the form of cracks and pores, as results of high percentage of carbon in the base metal. ...
Influence of welded joint microstructures on fatigue behaviour of specimens with a notch in the heat affected zone
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In this paper, the results of determining the Paris law coefficients, C and m, are presented, based on the experimental data obtained by three-point bending testing of 8 welded joint specimens. The specimens were taken ...