Tensile behaviour of polyethylene under different loading rates in the presence of imperfections
(Institut za ispitivanje materijala, Beograd, 2016)
This paper highlights the changes of polyethylene behaviour during various loading rates. The experimental programme was carried out on samples taken from PE80 polyethylene gas pipes with simulated imperfections with ...
Low-temperature corrosion damage and repair of boiler bottom panel tubes
(Institut za ispitivanje materijala, Beograd, 2017)
The method used for repairing of the bottom panel of hot water boiler of 30 MW power, manufactured by Remming (a part of the 'Valjevo' Heating Plant) is presented in this paper along with the reasons why damage has occurred. ...
Integrity assessment of regulation system pipeline elements in hydroelectric generating set a6 of hydro power plant 'djerdap 1'
(Institut za ispitivanje materijala, Beograd, 2016)
Vertical Kaplan turbines with nominal power of 176 MW manufactured in Russia are installed in 6 hydroelectric generating sets at hydro power plant 'Djerdap 1' (Kladovo, Serbia). Most of the components are made of materials ...
Numerical assessment of stress intensity factors at tips of multi-site cracks in unstiffened panel
(Institut za ispitivanje materijala, Beograd, 2017)
The aim of this paper is to establish and demonstrate diverse capacity and performances of different numerical methods for calculating stress intensity factors' (SIFs) histories versus crack length for problems involving ...
Assessment of integrity of pressure vessels for compressed air
(Institut za ispitivanje materijala, Beograd, 2021)
Fracture mechanics approach for structural integrity assessment is described in the case of pressure vessels for compressed air. The results of non-destructive testing indicated unacceptable defects on the vessels and set ...
Finite element analysis of fracture resistance parameters for stationary semi-elliptical surface cracks in high strength steel
(Institut za ispitivanje materijala, Beograd, 2015)
This study deals with numerical simulations based on elastic-plastic finite element method for nonlinear stress analyses on pre-cracked tensile specimens with high strength properties. The influence of crack geometry on ...
Advantages of friction stir welding over arc welding with respect to health and environmental protection and work safety [Prednosti zavarivanja trenjem sa mešanjem u odnosu na elektrolučno zavarivanje - Zaštita zdravlja i životne sredine i bezbednost na r
(Institut za ispitivanje materijala, Beograd, 2015)
In modern industrial production, every manufacturing and assembly process should be assessed with respect to its influence on the environment. For a company that invests in a new process, a careful analysis of HSE problems ...
Friction stir welding of aluminium alloys - T joints
(Institut za ispitivanje materijala, Beograd, 2015)
The paper presents results of research on the possibility of producing T-joints of aluminium alloys without defect by friction stir welding process. Friction stir welding process is applied in welding T-joints of aluminium ...
Final stretch zone width determination for MP35N multiphase alloy
(Institut za ispitivanje materijala, Beograd, 2015)
This paper presents an experimental elastic-plastic fracture behaviour analysis in order to evaluate a resistance of the aged and unaged MP35N alloy to stable and unstable crack growth. MP35N fracture behaviour has been ...
Integrity assessment of turbine flat cover pipe
(Institut za ispitivanje materijala, Beograd, 2018)
The turbine flat cover pipe (dimension phi 219.1x12.7 mm, and material STPG-38) is tested and cracks are found. Determination of the required wall thickness for a pipe exposed to internal pressure is done according to EN ...