High-density ceramics obtained by andesite basalt sintering
2022
Аутори
Pavkov, VladimirBakić, Gordana
Maksimović, Vesna
Cvijović-Alagić, Ivana
Prekajski-Dordjević, Marija
Bucevac, Dušan
Matović, Branko
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In the present study, andesite basalt originated from the deposit site ???Donje Jarinje???, Serbia, was examined as a potential raw material for high-density ceramics production. The production of high-density ceramics included dry milling, homogenization, cold isostatic pressing and sintering in the air. To determine the optimal processing parameters the sintering was conducted at 1040, 1050, 1060, 1070 and 1080 ??C, and afterwards the sintering duration was varied from 30 to 240 min at the optimal sintering temperature of 1060 ??C. Characterization of the starting and sintered materials included the estimation of particle size distribution, density, hardness and fracture toughness complemented with X-ray diffraction, optical light microscopy, scanning electron microscopy and energy dispersive spectroscopy analysis. Phase transformations did not occur during processing in the investigated temperature range from 1040 to 1080 ??C. The obtained research results showed that 99.5% of relat...ive density and the highest hardness and fracture toughness values of 6.7 GPa and 2.2 MPa??m1/2, respectively, were achieved for the andesite basalt sintered at 1060 ??C for 60 min in the air. The results of the present study confirmed that the sintered andesite basalt can be used as a high-density ceramic material for various industrial applications.
Кључне речи:
structural applications / sintering / optical microscopy / mechanical properties / andesite basaltИзвор:
Processing and Application of Ceramics, 2022, 16, 2, 143-152Издавач:
- Univerzitet u Novom Sadu - Tehnološki fakultet, Novi Sad
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200017 (Универзитет у Београду, Институт за нуклеарне науке Винча, Београд-Винча) (RS-MESTD-inst-2020-200017)
DOI: 10.2298/PAC2202143P
ISSN: 1820-6131
WoS: 000822705900007
Scopus: 2-s2.0-85135044131
Колекције
Институција/група
Mašinski fakultetTY - JOUR AU - Pavkov, Vladimir AU - Bakić, Gordana AU - Maksimović, Vesna AU - Cvijović-Alagić, Ivana AU - Prekajski-Dordjević, Marija AU - Bucevac, Dušan AU - Matović, Branko PY - 2022 UR - https://machinery.mas.bg.ac.rs/handle/123456789/3787 AB - In the present study, andesite basalt originated from the deposit site ???Donje Jarinje???, Serbia, was examined as a potential raw material for high-density ceramics production. The production of high-density ceramics included dry milling, homogenization, cold isostatic pressing and sintering in the air. To determine the optimal processing parameters the sintering was conducted at 1040, 1050, 1060, 1070 and 1080 ??C, and afterwards the sintering duration was varied from 30 to 240 min at the optimal sintering temperature of 1060 ??C. Characterization of the starting and sintered materials included the estimation of particle size distribution, density, hardness and fracture toughness complemented with X-ray diffraction, optical light microscopy, scanning electron microscopy and energy dispersive spectroscopy analysis. Phase transformations did not occur during processing in the investigated temperature range from 1040 to 1080 ??C. The obtained research results showed that 99.5% of relative density and the highest hardness and fracture toughness values of 6.7 GPa and 2.2 MPa??m1/2, respectively, were achieved for the andesite basalt sintered at 1060 ??C for 60 min in the air. The results of the present study confirmed that the sintered andesite basalt can be used as a high-density ceramic material for various industrial applications. PB - Univerzitet u Novom Sadu - Tehnološki fakultet, Novi Sad T2 - Processing and Application of Ceramics T1 - High-density ceramics obtained by andesite basalt sintering EP - 152 IS - 2 SP - 143 VL - 16 DO - 10.2298/PAC2202143P ER -
@article{ author = "Pavkov, Vladimir and Bakić, Gordana and Maksimović, Vesna and Cvijović-Alagić, Ivana and Prekajski-Dordjević, Marija and Bucevac, Dušan and Matović, Branko", year = "2022", abstract = "In the present study, andesite basalt originated from the deposit site ???Donje Jarinje???, Serbia, was examined as a potential raw material for high-density ceramics production. The production of high-density ceramics included dry milling, homogenization, cold isostatic pressing and sintering in the air. To determine the optimal processing parameters the sintering was conducted at 1040, 1050, 1060, 1070 and 1080 ??C, and afterwards the sintering duration was varied from 30 to 240 min at the optimal sintering temperature of 1060 ??C. Characterization of the starting and sintered materials included the estimation of particle size distribution, density, hardness and fracture toughness complemented with X-ray diffraction, optical light microscopy, scanning electron microscopy and energy dispersive spectroscopy analysis. Phase transformations did not occur during processing in the investigated temperature range from 1040 to 1080 ??C. The obtained research results showed that 99.5% of relative density and the highest hardness and fracture toughness values of 6.7 GPa and 2.2 MPa??m1/2, respectively, were achieved for the andesite basalt sintered at 1060 ??C for 60 min in the air. The results of the present study confirmed that the sintered andesite basalt can be used as a high-density ceramic material for various industrial applications.", publisher = "Univerzitet u Novom Sadu - Tehnološki fakultet, Novi Sad", journal = "Processing and Application of Ceramics", title = "High-density ceramics obtained by andesite basalt sintering", pages = "152-143", number = "2", volume = "16", doi = "10.2298/PAC2202143P" }
Pavkov, V., Bakić, G., Maksimović, V., Cvijović-Alagić, I., Prekajski-Dordjević, M., Bucevac, D.,& Matović, B.. (2022). High-density ceramics obtained by andesite basalt sintering. in Processing and Application of Ceramics Univerzitet u Novom Sadu - Tehnološki fakultet, Novi Sad., 16(2), 143-152. https://doi.org/10.2298/PAC2202143P
Pavkov V, Bakić G, Maksimović V, Cvijović-Alagić I, Prekajski-Dordjević M, Bucevac D, Matović B. High-density ceramics obtained by andesite basalt sintering. in Processing and Application of Ceramics. 2022;16(2):143-152. doi:10.2298/PAC2202143P .
Pavkov, Vladimir, Bakić, Gordana, Maksimović, Vesna, Cvijović-Alagić, Ivana, Prekajski-Dordjević, Marija, Bucevac, Dušan, Matović, Branko, "High-density ceramics obtained by andesite basalt sintering" in Processing and Application of Ceramics, 16, no. 2 (2022):143-152, https://doi.org/10.2298/PAC2202143P . .