Surface characteristics and cavitation damage progress in ductile materials
Samo za registrovane korisnike
2019
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
In this paper the investigation and analysis of ductile materials behavior under cavitation bubble collapsing are presented. Three ductile materials (Cu, AlMnMg-alloy, and St.St.316) were treated with cavitation. The cavitating jet generator was used as a tool to produce intensive, fast and severe cavitation phenomenon which is suitable for cavitation damage resistance study. The treated surfaces were characterized in detail by using different microscopy techniques and surface morphology analysis was done. The obtained result shows that the damage process is created by the shearing stress on the surface induced by microjets during cavity collapse. The mechanical properties of the material mainly "fatigue strength" and its Stacking Fault Energy (SFE) played a major role in the damage process. The cavitation damage based on exposure time period starts with surface hardening, followed by plastic deformation and finally by erosion and cracking as a consequence. The in-depth surface charact...erization using these microscopy techniques provides significant information for monitoring and understanding the cavitation damage mechanism and progress. Energy-dispersive X-ray spectroscopy (EDS) was used to measure the composition of the test materials which helps in the interpretation of the behavior of the material under the cavitation attack.
Ključne reči:
Erosion / Deformation / Crack / Collapse / CavitationIzvor:
Engineering Failure Analysis, 2019, 106Izdavač:
- Pergamon-Elsevier Science Ltd, Oxford
DOI: 10.1016/j.engfailanal.2019.104157
ISSN: 1350-6307
WoS: 000496192500022
Scopus: 2-s2.0-85071850872
Kolekcije
Institucija/grupa
Mašinski fakultetTY - JOUR AU - Hutli, Ezddin AU - Fekete, Tamas AU - Nedeljković, Miloš PY - 2019 UR - https://machinery.mas.bg.ac.rs/handle/123456789/3110 AB - In this paper the investigation and analysis of ductile materials behavior under cavitation bubble collapsing are presented. Three ductile materials (Cu, AlMnMg-alloy, and St.St.316) were treated with cavitation. The cavitating jet generator was used as a tool to produce intensive, fast and severe cavitation phenomenon which is suitable for cavitation damage resistance study. The treated surfaces were characterized in detail by using different microscopy techniques and surface morphology analysis was done. The obtained result shows that the damage process is created by the shearing stress on the surface induced by microjets during cavity collapse. The mechanical properties of the material mainly "fatigue strength" and its Stacking Fault Energy (SFE) played a major role in the damage process. The cavitation damage based on exposure time period starts with surface hardening, followed by plastic deformation and finally by erosion and cracking as a consequence. The in-depth surface characterization using these microscopy techniques provides significant information for monitoring and understanding the cavitation damage mechanism and progress. Energy-dispersive X-ray spectroscopy (EDS) was used to measure the composition of the test materials which helps in the interpretation of the behavior of the material under the cavitation attack. PB - Pergamon-Elsevier Science Ltd, Oxford T2 - Engineering Failure Analysis T1 - Surface characteristics and cavitation damage progress in ductile materials VL - 106 DO - 10.1016/j.engfailanal.2019.104157 ER -
@article{ author = "Hutli, Ezddin and Fekete, Tamas and Nedeljković, Miloš", year = "2019", abstract = "In this paper the investigation and analysis of ductile materials behavior under cavitation bubble collapsing are presented. Three ductile materials (Cu, AlMnMg-alloy, and St.St.316) were treated with cavitation. The cavitating jet generator was used as a tool to produce intensive, fast and severe cavitation phenomenon which is suitable for cavitation damage resistance study. The treated surfaces were characterized in detail by using different microscopy techniques and surface morphology analysis was done. The obtained result shows that the damage process is created by the shearing stress on the surface induced by microjets during cavity collapse. The mechanical properties of the material mainly "fatigue strength" and its Stacking Fault Energy (SFE) played a major role in the damage process. The cavitation damage based on exposure time period starts with surface hardening, followed by plastic deformation and finally by erosion and cracking as a consequence. The in-depth surface characterization using these microscopy techniques provides significant information for monitoring and understanding the cavitation damage mechanism and progress. Energy-dispersive X-ray spectroscopy (EDS) was used to measure the composition of the test materials which helps in the interpretation of the behavior of the material under the cavitation attack.", publisher = "Pergamon-Elsevier Science Ltd, Oxford", journal = "Engineering Failure Analysis", title = "Surface characteristics and cavitation damage progress in ductile materials", volume = "106", doi = "10.1016/j.engfailanal.2019.104157" }
Hutli, E., Fekete, T.,& Nedeljković, M.. (2019). Surface characteristics and cavitation damage progress in ductile materials. in Engineering Failure Analysis Pergamon-Elsevier Science Ltd, Oxford., 106. https://doi.org/10.1016/j.engfailanal.2019.104157
Hutli E, Fekete T, Nedeljković M. Surface characteristics and cavitation damage progress in ductile materials. in Engineering Failure Analysis. 2019;106. doi:10.1016/j.engfailanal.2019.104157 .
Hutli, Ezddin, Fekete, Tamas, Nedeljković, Miloš, "Surface characteristics and cavitation damage progress in ductile materials" in Engineering Failure Analysis, 106 (2019), https://doi.org/10.1016/j.engfailanal.2019.104157 . .