Comparative Exemination of the Strengthened and Non-Strengthened NIMONIC Specimens with Laser Shot Peening Method

Abstract

Laser shot peening (LSP) of material strengthening is nowdays widely used method in various branches of industry. In this paper are presented comparative exeminations of specimen made of NIMONIC and strengthened specimen on which laser shot peening method was performed. Specimens were made as thin plates with holes. Macrostructural surface tests were performed around the specimens holes with different magnifications for both specimens as well as certain damages on the specimens. 3D images of specimens damages provide insights into the its dimensions. In addition, the roughness of non-strengthed and strengthed specimens was also performed. Hardness tests using the Rockwell C method of both specimens show a difference in the hardness of both samples and the main characteristics of the laser shot peening method. Also, the analysis on how the damage of samples could represent the location of initial cracks that could cause failure of the specimens or generally machine part is given as well.