Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service
Само за регистроване кориснике
2017
Аутори
Bakić, GordanaĐukić, Miloš
Rajičić, Bratislav
Matić, M.
Maksimović, Vesna
Mitrović, Radivoje
Mišković, Žarko
Maslarević, Aleksandar
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In the past decades, tempered martensitic ferritic steels with 9-12% chromium and containing carbide stabilizing elements have been widely used for components which operate within the creep range in power and industrial processing plants. The investigated samples made of X20CrMoV12-1 steel were taken from the main steam pipeline in thermal power plant after 250.000 h (545°C and 19MPa). The low values of impact toughness are the consequence of aging and weakening of grain boundaries, despite the fact that aging processes have not significant effects on the microstructural degradation and drop of the other mechanical properties.
Извор:
ICF 2017 - 14th International Conference on Fracture, 2017, 1, 681-682Издавач:
- International Conference on Fracture
Scopus: 2-s2.0-85065962534
Институција/група
Inovacioni centarTY - CONF AU - Bakić, Gordana AU - Đukić, Miloš AU - Rajičić, Bratislav AU - Matić, M. AU - Maksimović, Vesna AU - Mitrović, Radivoje AU - Mišković, Žarko AU - Maslarević, Aleksandar PY - 2017 UR - https://machinery.mas.bg.ac.rs/handle/123456789/2672 AB - In the past decades, tempered martensitic ferritic steels with 9-12% chromium and containing carbide stabilizing elements have been widely used for components which operate within the creep range in power and industrial processing plants. The investigated samples made of X20CrMoV12-1 steel were taken from the main steam pipeline in thermal power plant after 250.000 h (545°C and 19MPa). The low values of impact toughness are the consequence of aging and weakening of grain boundaries, despite the fact that aging processes have not significant effects on the microstructural degradation and drop of the other mechanical properties. PB - International Conference on Fracture C3 - ICF 2017 - 14th International Conference on Fracture T1 - Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service EP - 682 SP - 681 VL - 1 UR - https://hdl.handle.net/21.15107/rcub_machinery_2672 ER -
@conference{ author = "Bakić, Gordana and Đukić, Miloš and Rajičić, Bratislav and Matić, M. and Maksimović, Vesna and Mitrović, Radivoje and Mišković, Žarko and Maslarević, Aleksandar", year = "2017", abstract = "In the past decades, tempered martensitic ferritic steels with 9-12% chromium and containing carbide stabilizing elements have been widely used for components which operate within the creep range in power and industrial processing plants. The investigated samples made of X20CrMoV12-1 steel were taken from the main steam pipeline in thermal power plant after 250.000 h (545°C and 19MPa). The low values of impact toughness are the consequence of aging and weakening of grain boundaries, despite the fact that aging processes have not significant effects on the microstructural degradation and drop of the other mechanical properties.", publisher = "International Conference on Fracture", journal = "ICF 2017 - 14th International Conference on Fracture", title = "Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service", pages = "682-681", volume = "1", url = "https://hdl.handle.net/21.15107/rcub_machinery_2672" }
Bakić, G., Đukić, M., Rajičić, B., Matić, M., Maksimović, V., Mitrović, R., Mišković, Ž.,& Maslarević, A.. (2017). Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service. in ICF 2017 - 14th International Conference on Fracture International Conference on Fracture., 1, 681-682. https://hdl.handle.net/21.15107/rcub_machinery_2672
Bakić G, Đukić M, Rajičić B, Matić M, Maksimović V, Mitrović R, Mišković Ž, Maslarević A. Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service. in ICF 2017 - 14th International Conference on Fracture. 2017;1:681-682. https://hdl.handle.net/21.15107/rcub_machinery_2672 .
Bakić, Gordana, Đukić, Miloš, Rajičić, Bratislav, Matić, M., Maksimović, Vesna, Mitrović, Radivoje, Mišković, Žarko, Maslarević, Aleksandar, "Material characterization of the main steam pipeline made of 12%Cr tempered martensite ferritic steel after prolonged service" in ICF 2017 - 14th International Conference on Fracture, 1 (2017):681-682, https://hdl.handle.net/21.15107/rcub_machinery_2672 .