Corrosion behavior of the as-cast and heat-treated ZA27 alloy
Апстракт
Corrosion behaviour of the as-cast and heat-treated ZA27 alloy was examined. The alloy was prepared by conventional melting and casting route and then thermally processed by applying T4 heat treatment regime (solutionizing at 370 °C for 3 hours followed by water quenching and natural aging). Corrosion rate of the as-cast and heat-treated ZA27 alloy was determined in 3.5 wt. % NaCl solution through immersion test using both weight loss method and polarization resistance measurements. It was shown that applied thermal treatment resulted in increased ductility of the heat-treated alloy and had a small beneficial effect on the corrosion resistance of ZA27 alloy.
Кључне речи:
ZA27 alloy / polarization resistance / microstructure / immersion test / heat treatment / corrosionИзвор:
Tribology in Industry, 2011, 33, 2, 87-93Издавач:
- Fakultet inženjerskih nauka, Kragujevac
Колекције
Институција/група
Mašinski fakultetTY - JOUR AU - Bobić, Biljana AU - Mitrović, Slobodan AU - Babić, Miroslav AU - Vencl, Aleksandar AU - Bobić, Ilija PY - 2011 UR - https://machinery.mas.bg.ac.rs/handle/123456789/1341 AB - Corrosion behaviour of the as-cast and heat-treated ZA27 alloy was examined. The alloy was prepared by conventional melting and casting route and then thermally processed by applying T4 heat treatment regime (solutionizing at 370 °C for 3 hours followed by water quenching and natural aging). Corrosion rate of the as-cast and heat-treated ZA27 alloy was determined in 3.5 wt. % NaCl solution through immersion test using both weight loss method and polarization resistance measurements. It was shown that applied thermal treatment resulted in increased ductility of the heat-treated alloy and had a small beneficial effect on the corrosion resistance of ZA27 alloy. PB - Fakultet inženjerskih nauka, Kragujevac T2 - Tribology in Industry T1 - Corrosion behavior of the as-cast and heat-treated ZA27 alloy EP - 93 IS - 2 SP - 87 VL - 33 UR - https://hdl.handle.net/21.15107/rcub_machinery_1341 ER -
@article{ author = "Bobić, Biljana and Mitrović, Slobodan and Babić, Miroslav and Vencl, Aleksandar and Bobić, Ilija", year = "2011", abstract = "Corrosion behaviour of the as-cast and heat-treated ZA27 alloy was examined. The alloy was prepared by conventional melting and casting route and then thermally processed by applying T4 heat treatment regime (solutionizing at 370 °C for 3 hours followed by water quenching and natural aging). Corrosion rate of the as-cast and heat-treated ZA27 alloy was determined in 3.5 wt. % NaCl solution through immersion test using both weight loss method and polarization resistance measurements. It was shown that applied thermal treatment resulted in increased ductility of the heat-treated alloy and had a small beneficial effect on the corrosion resistance of ZA27 alloy.", publisher = "Fakultet inženjerskih nauka, Kragujevac", journal = "Tribology in Industry", title = "Corrosion behavior of the as-cast and heat-treated ZA27 alloy", pages = "93-87", number = "2", volume = "33", url = "https://hdl.handle.net/21.15107/rcub_machinery_1341" }
Bobić, B., Mitrović, S., Babić, M., Vencl, A.,& Bobić, I.. (2011). Corrosion behavior of the as-cast and heat-treated ZA27 alloy. in Tribology in Industry Fakultet inženjerskih nauka, Kragujevac., 33(2), 87-93. https://hdl.handle.net/21.15107/rcub_machinery_1341
Bobić B, Mitrović S, Babić M, Vencl A, Bobić I. Corrosion behavior of the as-cast and heat-treated ZA27 alloy. in Tribology in Industry. 2011;33(2):87-93. https://hdl.handle.net/21.15107/rcub_machinery_1341 .
Bobić, Biljana, Mitrović, Slobodan, Babić, Miroslav, Vencl, Aleksandar, Bobić, Ilija, "Corrosion behavior of the as-cast and heat-treated ZA27 alloy" in Tribology in Industry, 33, no. 2 (2011):87-93, https://hdl.handle.net/21.15107/rcub_machinery_1341 .