Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection
Апстракт
The safe towing of aircraft is an important part in aviation security. Failures during the towing and parkingrelated operations are not so rare due to bad working circumstance, human error, etc. Tow bars are simplebut very important elements, for towing aircrafts on airports all over the world. This paper describesfailure analysis of accident during towing of regional ATR 72 aircraft. During towing of ATR 72 aircraftsudden fracture of shear pins caused that tow tractor goes into one and airplane ATR 72 into otherdirection. As a result, the airplane crashed on the empty tanker truck and severely deformed nose in thisground damage incident. Design of failed tow bar key elements and of susceptibility to corrosion wasdiscussed in this paper. Failure analysis unveil the several key elements that lead to fracture of shear pins: outdated design of towbar, improper maintenance and non-regular towing of aircraft. Combination of reduction of load capacityof shear pins induced by corrosion and im...pulse overloading caused premature fracture of the shear pins.and damage of ATR 72 aircraft. As a result of presented analysis the remedy was initiative for detailinspection of existing tow bars and redesign or purchasing the new ones. The results are presented.
Извор:
10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens, 2020, 75-76Колекције
Институција/група
Inovacioni centarTY - CONF AU - Atanasovska, Ivana AU - Momčilović, Dejan B. PY - 2020 UR - https://machinery.mas.bg.ac.rs/handle/123456789/7512 AB - The safe towing of aircraft is an important part in aviation security. Failures during the towing and parkingrelated operations are not so rare due to bad working circumstance, human error, etc. Tow bars are simplebut very important elements, for towing aircrafts on airports all over the world. This paper describesfailure analysis of accident during towing of regional ATR 72 aircraft. During towing of ATR 72 aircraftsudden fracture of shear pins caused that tow tractor goes into one and airplane ATR 72 into otherdirection. As a result, the airplane crashed on the empty tanker truck and severely deformed nose in thisground damage incident. Design of failed tow bar key elements and of susceptibility to corrosion wasdiscussed in this paper. Failure analysis unveil the several key elements that lead to fracture of shear pins: outdated design of towbar, improper maintenance and non-regular towing of aircraft. Combination of reduction of load capacityof shear pins induced by corrosion and impulse overloading caused premature fracture of the shear pins.and damage of ATR 72 aircraft. As a result of presented analysis the remedy was initiative for detailinspection of existing tow bars and redesign or purchasing the new ones. The results are presented. C3 - 10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens T1 - Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection EP - 76 SP - 75 UR - https://hdl.handle.net/21.15107/rcub_machinery_7512 ER -
@conference{ author = "Atanasovska, Ivana and Momčilović, Dejan B.", year = "2020", abstract = "The safe towing of aircraft is an important part in aviation security. Failures during the towing and parkingrelated operations are not so rare due to bad working circumstance, human error, etc. Tow bars are simplebut very important elements, for towing aircrafts on airports all over the world. This paper describesfailure analysis of accident during towing of regional ATR 72 aircraft. During towing of ATR 72 aircraftsudden fracture of shear pins caused that tow tractor goes into one and airplane ATR 72 into otherdirection. As a result, the airplane crashed on the empty tanker truck and severely deformed nose in thisground damage incident. Design of failed tow bar key elements and of susceptibility to corrosion wasdiscussed in this paper. Failure analysis unveil the several key elements that lead to fracture of shear pins: outdated design of towbar, improper maintenance and non-regular towing of aircraft. Combination of reduction of load capacityof shear pins induced by corrosion and impulse overloading caused premature fracture of the shear pins.and damage of ATR 72 aircraft. As a result of presented analysis the remedy was initiative for detailinspection of existing tow bars and redesign or purchasing the new ones. The results are presented.", journal = "10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens", title = "Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection", pages = "76-75", url = "https://hdl.handle.net/21.15107/rcub_machinery_7512" }
Atanasovska, I.,& Momčilović, D. B.. (2020). Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection. in 10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens, 75-76. https://hdl.handle.net/21.15107/rcub_machinery_7512
Atanasovska I, Momčilović DB. Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection. in 10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens. 2020;:75-76. https://hdl.handle.net/21.15107/rcub_machinery_7512 .
Atanasovska, Ivana, Momčilović, Dejan B., "Failure analysis of ATR 72 tow bar–opportunity for re-design for inspection" in 10th EASN Virtual International Conference on Innovation in Aviation & Space to the Satisfaction of the European Citizens (2020):75-76, https://hdl.handle.net/21.15107/rcub_machinery_7512 .