Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
2017
Autori
Pavlović, MarkoDojčinović, Marina
Martinović, Sanja
Vlahović, Milica
Stević, Zoran
Jovanović, Marina
Volkov-Husović, Tatjana
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.
Ključne reči:
zircon based ceramic / cavitation erosion / mass loss / image analysis / thermal imagingIzvor:
Science of Sintering, 2017, 49Finansiranje / projekti:
- Implementacija savremenijih tehničko-tehnoloških i ekoloških rešenja u postojećim proizvodnim sistemima Rudnika Bakra Bor i Rudnika Bakra Majdanpek (RS-MESTD-Technological Development (TD or TR)-33007)
- Sinteza, procesiranje i karakterizacija nanostrukturnih materijala za primenu u oblasti energije, mehaničkog inženjerstva, zaštite životne stredine i biomedicine (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Razvoj novih metodologija revitalizacije turbinske i hidromehaničke opreme hidroelektrana u zavisnosti od uzroka degradacije materijala (RS-MESTD-Technological Development (TD or TR)-35002)
- Nov pristup dizajniranju materijala za konverziju i skladištenje energije (RS-MESTD-Basic Research (BR or ON)-172060)
Kolekcije
Institucija/grupa
Inovacioni centarTY - JOUR AU - Pavlović, Marko AU - Dojčinović, Marina AU - Martinović, Sanja AU - Vlahović, Milica AU - Stević, Zoran AU - Jovanović, Marina AU - Volkov-Husović, Tatjana PY - 2017 UR - https://machinery.mas.bg.ac.rs/handle/123456789/7442 AB - Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected. T2 - Science of Sintering T1 - Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic VL - 49 DO - 10.2298/SOS1702175P ER -
@article{ author = "Pavlović, Marko and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Jovanović, Marina and Volkov-Husović, Tatjana", year = "2017", abstract = "Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.", journal = "Science of Sintering", title = "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic", volume = "49", doi = "10.2298/SOS1702175P" }
Pavlović, M., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z., Jovanović, M.,& Volkov-Husović, T.. (2017). Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering, 49. https://doi.org/10.2298/SOS1702175P
Pavlović M, Dojčinović M, Martinović S, Vlahović M, Stević Z, Jovanović M, Volkov-Husović T. Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering. 2017;49. doi:10.2298/SOS1702175P .
Pavlović, Marko, Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Jovanović, Marina, Volkov-Husović, Tatjana, "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic" in Science of Sintering, 49 (2017), https://doi.org/10.2298/SOS1702175P . .