Stringer effect on fatigue crack propagation in A2024-T351 aluminum alloy welded joint
(Elsevier Sci Ltd, Oxford, 2017)
This paper describes fatigue crack growth in a friction stir welded T joints made of aluminum alloy A2024-T351 under three point bending loads. For this purpose, three dimensional homogeneous isotropic model is used to ...
Analysis of welded tensile plates with a surface notch in the weld metal and heat affected zone
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The behavior of the plates with a surface notch under tensile external loading is experimentally and numerically analyzed. The specimens were made of micro-alloyed steel NIO-MOL 490 K. welded by MAC (CO2) welding method. ...
Mock-up testing facilities and qualification strategy for EU ITER TBMs
(Elsevier Science Sa, Lausanne, 2010)
European test blanket modules (TBM) for both European blanket concepts, namely the Helium Cooled Lithium Lead (HCLL) and the Helium Cooled Pebble Bed (HCPB), and their auxiliary systems have been designed in the last years. ...
Failure analysis of the combat jet aircraft rudder shaft
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
This paper analyzes failure causes of the combat jet aircraft rudder shaft (RS) which occurred during the flight mission. A finite element method (FEM), utilized to determine the stress state of the RS subjected to hinge ...
Bucket chain excavator: Failure analysis and redesign of the counterweight boom supporting truss columns
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The supporting truss of the counterweight boom is a vital part of the bucket chain excavator's (BCE) superstructure. The occurrence and propagation of cracks in the supporting truss columns' heads may lead to BCE collapse. ...
Austempering Kinetics of Cu-Ni Alloyed Austempered Ductile Iron
(Korean Inst Metals Materials, Seoul, 2014)
The aim of the paper was to investigate the effect of austempering parameters (time and temperature) on the microstructure and mechanical properties of ADI alloyed with 1.5% Cu and 1.6% Ni (in wt.%) in order to establish ...
The renewed TC12/ESIS technical committee - Risk analysis and safety of large structures and components
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The ESIS Executive Committee decided to nominate a new team for the leadership and management of the TC12/ESIS technical committee (TC), as well as update the TC name as "Risk Analysis and Safety of Large Structures and ...
Hydrogen Embrittlement of Industrial Components: Prediction, Prevention, and Models
(Natl Assoc Corrosion Eng, Houston, 2016)
Hydrogen embrittlement is a common, dangerous, and poorly understood cause of failure in many metal alloys. In practice, it is observed that different types of damage to industrial components have been tied to the presence ...
Fracture mechanics and fatigue crack propagation in armor steel welds
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The welding process of armor steel is a complex process due to possible welding faults appearing in all zones of weld metal joint in the form of cracks and pores, as results of high percentage of carbon in the base metal. ...
Thermal-hydraulics of helium cooled First Wall channels and scoping investigations on performance improvement by application of ribs and mixing devices
(Elsevier Science Sa, Lausanne, 2016)
The first wall (FW) of DEMO is a component with high thermal loads. The cooling of the FW has to comply with the material's upper and lower temperature limits and requirements from stress assessment, like low temperature ...