Dehydration of rhyolite: activation energy, water speciation and morphological investigation
Samo za registrovane korisnike
2020
Autori
Angelopoulos, Panagiotis M.Manić, Nebojša
Tsakiridis, Petros
Taxiarchou, Maria
Janković, Bojan
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Rhyolite is an extrusive, igneous rock of aluminosilicate composition that upon rapid cooling forms obsidian. Obsidian is amorphous and contains limited water portions ( lt 2 mass%); however, secondary hydration turns it either to perlite (H2O approximate to 2-5 mass%) or pitchstone (> 5 mass%). In the current study, kinetics of hydrous rhyolite dehydration were investigated by thermogravimetry up to 1000 degrees C, at heating rates of 2.5, 5, 10 and 20 degrees C min(-1)and under inert atmosphere. The mass loss is approx. 7.6 mass%, occurs along wide temperature range (100-800 degrees C) and is solely attributed to the release of molecular water ((H2O)(m)) and hydroxyl groups (OH). Rhyolite dehydration was considered as a solid-state reaction, and the apparent activation energy (E-a) of dehydration was calculated throughout the whole conversion range (a) by applying the isoconversional Friedman and advanced Vyazovkin methods. Both methods revealed inverse sigmoid trend in E(a)values v...ersus conversion degree, possessing almost stable value of 61 +/- 5 kJ mol(-1)for Friedman method and 59.44 kJ mol(-1)for Vyazovkin method on conversion range between 0.25 and 0.75, and sharp increase at higher conversion degree. The intensive change inE(a)during dehydration progression is attributed to the change in releasing species (from (H2O)(m)to OH). Raman and FT-IR spectroscopy analyses of raw and partially dehydrated samples at different stages revealed that up to 300 degrees C mainly (H2O)(m)is diffused out of the material causing sample enrichment in OH groups. OH release, which occurs at relatively higher temperature, is accompanied by increase in apparent E(a)value of dehydration. Concerning microstructure of raw rhyolite, it exhibits a network of micro-fractures which serve as water release routes. Upon heating, more and wider fractures are created. At 600 degrees C, fractures merging occurs creating voids, which constitute forerunners of the expansion phenomenon. Further temperature increase causes material softening allowing local plastic deformation, which under the high pressure that is exerted by the releasing water species incites the formation of large cavities and fractures, initiating expansion.
Ključne reči:
Volcanic glass dehydration / Isoconversional methods / Hydrous rhyolite / Expanded perlite / Dehydroxylation / Activation energyIzvor:
Journal of Thermal Analysis and Calorimetry, 2020, 142, 1, 395-407Izdavač:
- Springer, Dordrecht
DOI: 10.1007/s10973-020-10105-2
ISSN: 1388-6150
WoS: 000556688000003
Scopus: 2-s2.0-85089090806
Kolekcije
Institucija/grupa
Mašinski fakultetTY - JOUR AU - Angelopoulos, Panagiotis M. AU - Manić, Nebojša AU - Tsakiridis, Petros AU - Taxiarchou, Maria AU - Janković, Bojan PY - 2020 UR - https://machinery.mas.bg.ac.rs/handle/123456789/3409 AB - Rhyolite is an extrusive, igneous rock of aluminosilicate composition that upon rapid cooling forms obsidian. Obsidian is amorphous and contains limited water portions ( lt 2 mass%); however, secondary hydration turns it either to perlite (H2O approximate to 2-5 mass%) or pitchstone (> 5 mass%). In the current study, kinetics of hydrous rhyolite dehydration were investigated by thermogravimetry up to 1000 degrees C, at heating rates of 2.5, 5, 10 and 20 degrees C min(-1)and under inert atmosphere. The mass loss is approx. 7.6 mass%, occurs along wide temperature range (100-800 degrees C) and is solely attributed to the release of molecular water ((H2O)(m)) and hydroxyl groups (OH). Rhyolite dehydration was considered as a solid-state reaction, and the apparent activation energy (E-a) of dehydration was calculated throughout the whole conversion range (a) by applying the isoconversional Friedman and advanced Vyazovkin methods. Both methods revealed inverse sigmoid trend in E(a)values versus conversion degree, possessing almost stable value of 61 +/- 5 kJ mol(-1)for Friedman method and 59.44 kJ mol(-1)for Vyazovkin method on conversion range between 0.25 and 0.75, and sharp increase at higher conversion degree. The intensive change inE(a)during dehydration progression is attributed to the change in releasing species (from (H2O)(m)to OH). Raman and FT-IR spectroscopy analyses of raw and partially dehydrated samples at different stages revealed that up to 300 degrees C mainly (H2O)(m)is diffused out of the material causing sample enrichment in OH groups. OH release, which occurs at relatively higher temperature, is accompanied by increase in apparent E(a)value of dehydration. Concerning microstructure of raw rhyolite, it exhibits a network of micro-fractures which serve as water release routes. Upon heating, more and wider fractures are created. At 600 degrees C, fractures merging occurs creating voids, which constitute forerunners of the expansion phenomenon. Further temperature increase causes material softening allowing local plastic deformation, which under the high pressure that is exerted by the releasing water species incites the formation of large cavities and fractures, initiating expansion. PB - Springer, Dordrecht T2 - Journal of Thermal Analysis and Calorimetry T1 - Dehydration of rhyolite: activation energy, water speciation and morphological investigation EP - 407 IS - 1 SP - 395 VL - 142 DO - 10.1007/s10973-020-10105-2 ER -
@article{ author = "Angelopoulos, Panagiotis M. and Manić, Nebojša and Tsakiridis, Petros and Taxiarchou, Maria and Janković, Bojan", year = "2020", abstract = "Rhyolite is an extrusive, igneous rock of aluminosilicate composition that upon rapid cooling forms obsidian. Obsidian is amorphous and contains limited water portions ( lt 2 mass%); however, secondary hydration turns it either to perlite (H2O approximate to 2-5 mass%) or pitchstone (> 5 mass%). In the current study, kinetics of hydrous rhyolite dehydration were investigated by thermogravimetry up to 1000 degrees C, at heating rates of 2.5, 5, 10 and 20 degrees C min(-1)and under inert atmosphere. The mass loss is approx. 7.6 mass%, occurs along wide temperature range (100-800 degrees C) and is solely attributed to the release of molecular water ((H2O)(m)) and hydroxyl groups (OH). Rhyolite dehydration was considered as a solid-state reaction, and the apparent activation energy (E-a) of dehydration was calculated throughout the whole conversion range (a) by applying the isoconversional Friedman and advanced Vyazovkin methods. Both methods revealed inverse sigmoid trend in E(a)values versus conversion degree, possessing almost stable value of 61 +/- 5 kJ mol(-1)for Friedman method and 59.44 kJ mol(-1)for Vyazovkin method on conversion range between 0.25 and 0.75, and sharp increase at higher conversion degree. The intensive change inE(a)during dehydration progression is attributed to the change in releasing species (from (H2O)(m)to OH). Raman and FT-IR spectroscopy analyses of raw and partially dehydrated samples at different stages revealed that up to 300 degrees C mainly (H2O)(m)is diffused out of the material causing sample enrichment in OH groups. OH release, which occurs at relatively higher temperature, is accompanied by increase in apparent E(a)value of dehydration. Concerning microstructure of raw rhyolite, it exhibits a network of micro-fractures which serve as water release routes. Upon heating, more and wider fractures are created. At 600 degrees C, fractures merging occurs creating voids, which constitute forerunners of the expansion phenomenon. Further temperature increase causes material softening allowing local plastic deformation, which under the high pressure that is exerted by the releasing water species incites the formation of large cavities and fractures, initiating expansion.", publisher = "Springer, Dordrecht", journal = "Journal of Thermal Analysis and Calorimetry", title = "Dehydration of rhyolite: activation energy, water speciation and morphological investigation", pages = "407-395", number = "1", volume = "142", doi = "10.1007/s10973-020-10105-2" }
Angelopoulos, P. M., Manić, N., Tsakiridis, P., Taxiarchou, M.,& Janković, B.. (2020). Dehydration of rhyolite: activation energy, water speciation and morphological investigation. in Journal of Thermal Analysis and Calorimetry Springer, Dordrecht., 142(1), 395-407. https://doi.org/10.1007/s10973-020-10105-2
Angelopoulos PM, Manić N, Tsakiridis P, Taxiarchou M, Janković B. Dehydration of rhyolite: activation energy, water speciation and morphological investigation. in Journal of Thermal Analysis and Calorimetry. 2020;142(1):395-407. doi:10.1007/s10973-020-10105-2 .
Angelopoulos, Panagiotis M., Manić, Nebojša, Tsakiridis, Petros, Taxiarchou, Maria, Janković, Bojan, "Dehydration of rhyolite: activation energy, water speciation and morphological investigation" in Journal of Thermal Analysis and Calorimetry, 142, no. 1 (2020):395-407, https://doi.org/10.1007/s10973-020-10105-2 . .