Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering
Nema prikaza
Autori
Obradović, NinaPavlović, Vera P.
Kachlik, Martin
Maca, Karel
Olćan, Dragan
Đorđević, Antonije
Tshantshapanyan, Ani
Vlahović, Branislav
Pavlović, Vladimir B.
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.
Ključne reči:
TeO2 / sintering / Mechanical activation / electrical properties / cordieriteIzvor:
Advances in Applied Ceramics, 2019, 118, 5, 241-248Izdavač:
- Taylor & Francis Ltd, Abingdon
Finansiranje / projekti:
- Usmerena sinteza, struktura i svojstva multifunkcionalnih materijala (RS-MESTD-Basic Research (BR or ON)-172057)
- National Science Foundation (NSF) [HRD-1345219, DMR-1523617]
- National Aeronautics and Space Administration (NASA) [NNX09AV07A]
- Czech Science Foundation (GACR) [17-05620S]
- Ministry of Education, Youth and Sports (MEYS) of CR: CEITEC 2020 [LQ1601]
Napomena:
- Peer-reviewed version of the article: https://machinery.mas.bg.ac.rs/handle/123456789/4058
Povezane informacije:
- Druga verzija
https://machinery.mas.bg.ac.rs/handle/123456789/4058
DOI: 10.1080/17436753.2018.1548150
ISSN: 1743-6753
WoS: 000470329400001
Scopus: 2-s2.0-85057585838
Kolekcije
Institucija/grupa
Mašinski fakultetTY - JOUR AU - Obradović, Nina AU - Pavlović, Vera P. AU - Kachlik, Martin AU - Maca, Karel AU - Olćan, Dragan AU - Đorđević, Antonije AU - Tshantshapanyan, Ani AU - Vlahović, Branislav AU - Pavlović, Vladimir B. PY - 2019 UR - https://machinery.mas.bg.ac.rs/handle/123456789/3138 AB - Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data. PB - Taylor & Francis Ltd, Abingdon T2 - Advances in Applied Ceramics T1 - Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering EP - 248 IS - 5 SP - 241 VL - 118 DO - 10.1080/17436753.2018.1548150 ER -
@article{ author = "Obradović, Nina and Pavlović, Vera P. and Kachlik, Martin and Maca, Karel and Olćan, Dragan and Đorđević, Antonije and Tshantshapanyan, Ani and Vlahović, Branislav and Pavlović, Vladimir B.", year = "2019", abstract = "Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.", publisher = "Taylor & Francis Ltd, Abingdon", journal = "Advances in Applied Ceramics", title = "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering", pages = "248-241", number = "5", volume = "118", doi = "10.1080/17436753.2018.1548150" }
Obradović, N., Pavlović, V. P., Kachlik, M., Maca, K., Olćan, D., Đorđević, A., Tshantshapanyan, A., Vlahović, B.,& Pavlović, V. B.. (2019). Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics Taylor & Francis Ltd, Abingdon., 118(5), 241-248. https://doi.org/10.1080/17436753.2018.1548150
Obradović N, Pavlović VP, Kachlik M, Maca K, Olćan D, Đorđević A, Tshantshapanyan A, Vlahović B, Pavlović VB. Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics. 2019;118(5):241-248. doi:10.1080/17436753.2018.1548150 .
Obradović, Nina, Pavlović, Vera P., Kachlik, Martin, Maca, Karel, Olćan, Dragan, Đorđević, Antonije, Tshantshapanyan, Ani, Vlahović, Branislav, Pavlović, Vladimir B., "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering" in Advances in Applied Ceramics, 118, no. 5 (2019):241-248, https://doi.org/10.1080/17436753.2018.1548150 . .