Screen printed barium titanate thick films prepared from mechanically activated powders
Нема приказа
Аутори
Stojanović, Biljana D.Foschini, C.R.
Pejović, V.Z.
Pavlović, Vladimir B.
Pavlović, Vera P.
Varela, J.A.
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Barium titanate thick films were prepared from mechanically activated powders based on BaCO3 and TiO2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported.
Кључне речи:
Thick films / Screen-printed / Properties / Microstructure / Barium titanateИзвор:
Key Engineering Materials, 2002, 206-213, II, 1425-1428Издавач:
- Trans Tech Publications Ltd
Колекције
Институција/група
Mašinski fakultetTY - JOUR AU - Stojanović, Biljana D. AU - Foschini, C.R. AU - Pejović, V.Z. AU - Pavlović, Vladimir B. AU - Pavlović, Vera P. AU - Varela, J.A. PY - 2002 UR - https://machinery.mas.bg.ac.rs/handle/123456789/218 AB - Barium titanate thick films were prepared from mechanically activated powders based on BaCO3 and TiO2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported. PB - Trans Tech Publications Ltd T2 - Key Engineering Materials T1 - Screen printed barium titanate thick films prepared from mechanically activated powders EP - 1428 IS - II SP - 1425 VL - 206-213 UR - https://hdl.handle.net/21.15107/rcub_machinery_218 ER -
@article{ author = "Stojanović, Biljana D. and Foschini, C.R. and Pejović, V.Z. and Pavlović, Vladimir B. and Pavlović, Vera P. and Varela, J.A.", year = "2002", abstract = "Barium titanate thick films were prepared from mechanically activated powders based on BaCO3 and TiO2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported.", publisher = "Trans Tech Publications Ltd", journal = "Key Engineering Materials", title = "Screen printed barium titanate thick films prepared from mechanically activated powders", pages = "1428-1425", number = "II", volume = "206-213", url = "https://hdl.handle.net/21.15107/rcub_machinery_218" }
Stojanović, B. D., Foschini, C.R., Pejović, V.Z., Pavlović, V. B., Pavlović, V. P.,& Varela, J.A.. (2002). Screen printed barium titanate thick films prepared from mechanically activated powders. in Key Engineering Materials Trans Tech Publications Ltd., 206-213(II), 1425-1428. https://hdl.handle.net/21.15107/rcub_machinery_218
Stojanović BD, Foschini C, Pejović V, Pavlović VB, Pavlović VP, Varela J. Screen printed barium titanate thick films prepared from mechanically activated powders. in Key Engineering Materials. 2002;206-213(II):1425-1428. https://hdl.handle.net/21.15107/rcub_machinery_218 .
Stojanović, Biljana D., Foschini, C.R., Pejović, V.Z., Pavlović, Vladimir B., Pavlović, Vera P., Varela, J.A., "Screen printed barium titanate thick films prepared from mechanically activated powders" in Key Engineering Materials, 206-213, no. II (2002):1425-1428, https://hdl.handle.net/21.15107/rcub_machinery_218 .