AB  - Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.
PB  - Taylor & Francis Ltd, Abingdon
T2  - Advances in Applied Ceramics
T1  - Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering
EP  - 248
IS  - 5
SP  - 241
VL  - 118
DO  - 10.1080/17436753.2018.1548150
ER  - 

@article{
author = "Obradović, Nina and Pavlović, Vera P. and Kachlik, Martin and Maca, Karel and Olćan, Dragan and Đorđević, Antonije and Tshantshapanyan, Ani and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2019",
abstract = "Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.",
publisher = "Taylor & Francis Ltd, Abingdon",
journal = "Advances in Applied Ceramics",
title = "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering",
pages = "248-241",
number = "5",
volume = "118",
doi = "10.1080/17436753.2018.1548150"
}

Obradović, N., Pavlović, V. P., Kachlik, M., Maca, K., Olćan, D., Đorđević, A., Tshantshapanyan, A., Vlahović, B.,& Pavlović, V. B.. (2019). Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics
Taylor & Francis Ltd, Abingdon., 118(5), 241-248.
https://doi.org/10.1080/17436753.2018.1548150

Obradović N, Pavlović VP, Kachlik M, Maca K, Olćan D, Đorđević A, Tshantshapanyan A, Vlahović B, Pavlović VB. Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics. 2019;118(5):241-248.
doi:10.1080/17436753.2018.1548150 .

Obradović, Nina, Pavlović, Vera P., Kachlik, Martin, Maca, Karel, Olćan, Dragan, Đorđević, Antonije, Tshantshapanyan, Ani, Vlahović, Branislav, Pavlović, Vladimir B., "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering" in Advances in Applied Ceramics, 118, no. 5 (2019):241-248,
https://doi.org/10.1080/17436753.2018.1548150 . .

TY  - JOUR
AU  - Obradović, Nina
AU  - Pavlović, Vera P.
AU  - Kachlik, Martin
AU  - Maca, Karel
AU  - Olćan, Dragan
AU  - Đorđević, Antonije
AU  - Tshantshapanyan, Ani
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - https://machinery.mas.bg.ac.rs/handle/123456789/4058
AB  - Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.
PB  - Taylor and Francis
T2  - Advances in Applied Ceramics
T1  - Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering
EP  - 248
IS  - 5
SP  - 241
VL  - 118
DO  - 10.1080/17436753.2018.1548150
ER  - 

@article{
author = "Obradović, Nina and Pavlović, Vera P. and Kachlik, Martin and Maca, Karel and Olćan, Dragan and Đorđević, Antonije and Tshantshapanyan, Ani and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2019",
abstract = "Sintering of pure cordierite 2MgO:2Al(2)O(3):5SiO(2), and cordierite with the addition of 5 mass % TeO2 was studied. Green bodies were prepared from powder mixtures mechanically activated in a high-energy planetary mill, shaped by uniaxial (20 MPa) and cold isostatic pressing (1000 MPa). The pressure-less sintering of these specimens was performed at 1350 degrees C for 1 h. High relative density over 95% of the theoretical value was obtained through solid-state reaction and pressure-less sintering of powder activated for 40 min, and for the first time reported in the literature. Phase composition and microstructures of sintered samples were determined by XRD and SEM, coupled with EDS mapping. The real part of the complex relative permittivity of the samples was measured at 200 MHz. The loss tangent of all samples was below the resolution of the measurement setup. A strong correlation between the relative permittivity and the density agrees with previously published data.",
publisher = "Taylor and Francis",
journal = "Advances in Applied Ceramics",
title = "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering",
pages = "248-241",
number = "5",
volume = "118",
doi = "10.1080/17436753.2018.1548150"
}

Obradović, N., Pavlović, V. P., Kachlik, M., Maca, K., Olćan, D., Đorđević, A., Tshantshapanyan, A., Vlahović, B.,& Pavlović, V. B.. (2019). Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics
Taylor and Francis., 118(5), 241-248.
https://doi.org/10.1080/17436753.2018.1548150

Obradović N, Pavlović VP, Kachlik M, Maca K, Olćan D, Đorđević A, Tshantshapanyan A, Vlahović B, Pavlović VB. Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering. in Advances in Applied Ceramics. 2019;118(5):241-248.
doi:10.1080/17436753.2018.1548150 .

Obradović, Nina, Pavlović, Vera P., Kachlik, Martin, Maca, Karel, Olćan, Dragan, Đorđević, Antonije, Tshantshapanyan, Ani, Vlahović, Branislav, Pavlović, Vladimir B., "Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering" in Advances in Applied Ceramics, 118, no. 5 (2019):241-248,
https://doi.org/10.1080/17436753.2018.1548150 . .